牌号信息	Durethan® BKV 230 DUS008 000000 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货	Durethan® BKV230W1 000000 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Durethan® BKV 230 DUS008 000000 含有30%的玻璃纤维PA 6材料，用注射成型方式进行加工，具有良好的抗冲击性能。 Durethan® BKV230 000000 DUS008 (Dry) PA 6, 30 % glass fibers, injection molding, improved impact strength Durethan® BKV230 000000 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength Durethan® BKV230 000000 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength	PA 6-共聚物，30%玻璃纤维，注塑，提高冲击强度，耐候性 Durethan® BKV230W1 000000 (Dry) PA 6-Copolymer, 30 % glass fibers, injection molding, improved impact strength, weather stabilized Durethan® BKV230W1 000000 PA 6-Copolymer, 30 % glass fibers, injection molding, improved impact strength, weather stabilized

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 30	玻璃纤维 30
用途：
性能特点：	冲击性能好,耐老化,热稳定性好 High impact resistance,Good heat aging resistance,Heat Stabilized	共聚物,耐候抗UV,冲击性能好 Copolymer,Weather resistance is good,High impact resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：120℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD：280℃，2.0 mm)
Shrinkage rate %

收缩率(MD：280℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：280℃，2.0 mm)
Shrinkage rate %

收缩率(TD：280℃，2.0 mm)
Shrinkage rate % ISO 294-4

表观密度
Apparent density g/cm³

机械性能
MECHANICAL Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.50% 应变)
bending strength MPa ISO 178-A

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain %

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

球压硬度
Ball hardness MPa

冲击性能
IMPACT Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

补充信息
Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

ISO Shortname
ISO Shortname ISO 1874

电气性能
ELECTRICAL Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm

体积电阻率(23℃)
Volume resistivity ohms·cm

相对电容率(23℃，1 MHz)
Relative permittivity

相对电容率(23℃，100 Hz)
Relative permittivity

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V

耗散因数(23℃，1 MHz)
Dissipation factor

耗散因数(23℃，100 Hz)
Dissipation factor

加工方式

注射 Durethan® BKV 230 DUS008 000000 Durethan® BKV230W1 000000 单位测试方法

Residual Moisture Content %

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 60x60x2; MT 80°C; 600 Bar

3 60x60x2mm, 80°C MT, 600 bar

4 60x60x2

5 60x60x2mm

6 0.079 in/min

7 2 mm/min

8 Pull Rate: 2 mm/min; 50% RH

9 10°C/min

2. 60x60x2mm, 4 hr

3. 60x60x2mm, 80°C MT, 600 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
电气性能
加工方式
注射
备注
返回顶部

PA6，Durethan® BKV 230 DUS008 000000对比PA6，Durethan® BKV230W1 000000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别