PC，LNP™ LUBRICOMP™ DL0029E compound对比PC，LNP™ LUBRICOMP™ DL002P compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ DL0029E compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ DL002P compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Lubricomp DL0029E化合物LNP LubricompDL0029E是一种基于聚碳酸酯树脂的化合物，含有10%的聚四氟乙烯。这种材料的附加特性包括：耐磨、阻燃。也称为：LNPLubricomp化合物DL-4020 FR产品再订购名称：DL0029ELNP Lubricomp DL0029E化合物LNP Lubricomp DL0029E是一种基于含聚四氟乙烯的聚碳酸酯树脂的化合物。这种材料的附加特性包括：阻燃性。也称为：lnplubricomp化合物dl-4020 fr产品再订购名称：dl0029e LNP™ LUBRICOMP™ DL0029E compound LNP LUBRICOMP DL0029E is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Wear Resistant, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DL-4020 FR Product reorder name: DL0029E LNP™ LUBRICOMP™ DL0029E compound LNP LUBRICOMP DL0029E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DL-4020 FR Product reorder name: DL0029E	LNP Lubricomp DL002P化合物LNP LubricompDL002P是一种基于聚碳酸酯树脂的化合物，含有10%的聚四氟乙烯。这种材料的附加功能包括：特殊加工，耐磨。也称为：LNPLubricomp化合物DL-4020 EP产品再订购名称：DL002PLNP Lubricomp DL002P化合物LNP LubricompDL002P是基于含聚四氟乙烯的聚碳酸酯树脂的化合物。这种材料的附加特性包括：特殊加工。也称为：LNPLubricomp化合物DL-4020 EP产品再订购名称：DL002P LNP™ LUBRICOMP™ DL002P compound LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4020 EP Product reorder name: DL002P LNP™ LUBRICOMP™ DL002P compound LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing. Also known as: LNP* LUBRICOMP* Compound DL-4020 EP Product reorder name: DL002P

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	PTFE 10	PTFE 10
用途：
性能特点：	阻燃,润滑性,耐磨,防火阻燃等级V-0 Flame Characteristics,Lubricating,Good wear resistance,V-0	易加工,润滑性,耐磨 Excellent Processability,Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ASTM D4812

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

阻燃性能
FLAMMABILITY LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位
UNIT 测试方法
TEST METHOD

1.90 mm
1.90 mm UL 94

加工方式

注射 LNP™ LUBRICOMP™ DL0029E compound LNP™ LUBRICOMP™ DL002P compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2.0 in/min

4 类型 1, 0.20 in/min

5 0.051 in/min

6 0.079 in/min

7 Yield

8 2 mm/min

9 80*10*4

10 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注