PP，SLOVALEN® PH 92 T 30对比PP，MAJORIS FT303 - 1451物性表,价格行情_搜料

牌号信息	SLOVALEN® PH 92 T 30 物性表 PP & 斯洛伐克Plastcom 指导价格：暂无塑料库存：缺货	MAJORIS FT303 - 1451 物性表 PP & 法国AD Majoris 指导价格：暂无塑料库存：缺货
牌号简介	改性聚丙烯注模，矿物填充量30%。增加了刚性、强度和热性能。收缩率降低。一般应用于各行业分支机构。 Modified PP for injection moulding with the content of 30% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. General application in all industry branches.	FT303-1451是一种30%的矿物填充聚丙烯化合物，用于注塑成型。该产品为天然FT303，但可根据要求提供其他颜色。FT303-1451特别适用于需要高耐洗洁剂性和热稳定性的应用。这就要求高流动性和良好的加工能力以及高尺寸稳定性。应用洗衣机配件洗碗机配件家用电器 FT303 - 1451 is a 30% mineral filled polypropylene compound intended for injection moulding. The product is available in natural FT303 but other colours can be provided on request. FT303 - 1451 has been developed especially for applications requiring high detergent resistance and heat stability. That requires high flow and good process ability and high dimensional stability. APPLICATIONS Washing machine parts Dishwasher components Household appliances

产品描述
厂家：	斯洛伐克Plastcom	法国AD Majoris
类别：	PP PP not specified	PP PP not specified
填料：	矿物 30	矿物 30
用途：	通用	电器用具,家电部件
性能特点：	机械强度好,收缩性低,耐热性好,热稳定性好,防火阻燃等级HB Good Rigidity,Low contractility,Heat Resistance, Good,Heat Stabilized,HB	易加工,尺寸稳定性好,流动性高,可回收,热稳定性好,耐洗涤剂,防火阻燃等级HB Excellent Processability,Good Dimensional Stability,High liquidity,Renewable resources,Heat Stabilized,Resistance to detergents,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位
UNIT 测试方法
TEST METHOD

含水量
water content % ISO 960

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

收缩率(MD)
Shrinkage rate % STM 64 0808

收缩率(TD)
Shrinkage rate % STM 64 0808

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B

阻燃性能
FLAMMABILITY SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位
UNIT 测试方法
TEST METHOD

灼热丝起燃温度
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级
Flame retardant level UL 94

加工方式

注射 SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度 SLOVALEN® PH 92 T 30 MAJORIS FT303 - 1451 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 50 mm/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
注射速度
备注