PA66，LNP™ LUBRICOMP™ RAL22I compound对比PA66，LNP™ LUBRICOMP™ RAL22S compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ RAL22I compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ RAL22S compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Lubricomp_RAL22I化合物LNP Lubricomp RAL22I是一种基于尼龙66树脂的化合物，含有10%聚四氟乙烯、10%芳纶纤维。这种材料的附加功能包括：耐磨，高冲击。也称为：LNPLubricomp化合物RAL-4022 HI产品再订购名称：RAL22ILNP Lubricomp RAL22I化合物LNP Lubricomp RAL22I是一种基于尼龙66树脂的化合物，含有聚四氟乙烯、芳纶纤维。这种材料的附加特性包括：内部润滑，高冲击。也称为：LNPLubricomp化合物RAL-4022 HI产品再订购名称：RAL22I LNP™ LUBRICOMP™ RAL22I compound LNP LUBRICOMP RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact. Also known as: LNP* LUBRICOMP* Compound RAL-4022 HI Product reorder name: RAL22I LNP™ LUBRICOMP™ RAL22I compound LNP LUBRICOMP RAL22I is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated, High Impact. Also known as: LNP* LUBRICOMP* Compound RAL-4022 HI Product reorder name: RAL22I	LNP Lubricomp_RAL22S化合物LNP Lubricomp RAL22S是一种基于尼龙66树脂的化合物，含有10%聚四氟乙烯、10%芳纶。这种材料的附加特性包括：耐磨性。也称为：LNPLubricomp化合物RAL-4022 HS产品再订购名称：RAL22SLNP Lubricomp RAL22S化合物LNP Lubricomp RAL22S是一种基于尼龙66树脂的化合物，含有聚四氟乙烯、芳纶纤维。这种材料的附加特性包括：内部润滑。也称为：LNPLubricomp化合物RAL-4022 HS产品再订购名称：RAL22S LNP™ LUBRICOMP™ RAL22S compound LNP LUBRICOMP RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4022 HS Product reorder name: RAL22S LNP™ LUBRICOMP™ RAL22S compound LNP LUBRICOMP RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RAL-4022 HS Product reorder name: RAL22S

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PA66 PA66	PA66 PA66
填料：	PTFE 10	PTFE 10
用途：
性能特点：	冲击性能好,润滑性,耐磨 High impact resistance,Lubricating,Good wear resistance	润滑性,耐磨 Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ RAL22I compound LNP™ LUBRICOMP™ RAL22S compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ RAL22I compound LNP™ LUBRICOMP™ RAL22S compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ RAL22I compound LNP™ LUBRICOMP™ RAL22S compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ RAL22I compound LNP™ LUBRICOMP™ RAL22S compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

加工方式

注射 LNP™ LUBRICOMP™ RAL22I compound LNP™ LUBRICOMP™ RAL22S compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

PA66，LNP™ LUBRICOMP™ RAL22I compound对比PA66，LNP™ LUBRICOMP™ RAL22S compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别