PA66，Ultramid® A3L BK7793对比PA66，Vydyne® 67B物性表,价格行情_搜料

牌号信息	Ultramid® A3L BK7793 物性表 PA66 & 德国巴斯夫指导价格：暂无塑料库存： 7700kg	Vydyne® 67B 物性表 PA66 & 美国奥升德指导价格：暂无塑料库存：缺货
牌号简介	Ultramid® A3L BK7793是一种冲击改性，热稳定的尼龙66注塑成型。该等级具有良好的表面外观，设计用于提供优异的耐刮性和抗损伤性。应用Ultramid® A3L BK7793可用于仪表板嵌框和车门嵌框等汽车内部应用。 Ultramid A3L BK7793 is an impact modified, heat stabilized polyamide 66 for injection molding. This grade has excellent surface appearance and was designed to offer exceptional scratch and mar resistance. Applications Ultramid A3L BK7793 can be used in automotive interior applications such as instrument panel bezels and door bezels.	Vydyne® 67B是一种非常高粘度的PA66树脂，适用于注塑和挤出应用。它只提供自然色。Vydyne® 67B树脂具有高强度、刚度和韧性，适用范围广泛，对各种化学品、溶剂和油具有良好的耐流体性。典型应用/最终用途：典型用途包括包装膜、单丝、刚毛、杆、管、片材和挤压型材。 Vydyne 67B is a very-high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67B resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils.

产品描述
厂家：	德国巴斯夫 BASF	美国奥升德 Ascend
类别：	PA66 PA66	PA66 PA66
填料：
用途：	汽车内部零件,汽车仪表板	棒材,工业应用,薄膜,型材,片材,单丝,管件
性能特点：	表面光泽度好,冲击性能好,耐油,耐刮擦,热稳定性好 Good surface appearance,High impact resistance,Grease resistance,High scratch resistance,Heat Stabilized	机械强度好,韧性好,高粘度,耐油,耐化学性,耐汽油,熔体稳定性高 Good Rigidity,Good flexibility,High Viscosity,Grease resistance,Solvent resistance,Gasoline resistance,Higher melt stability
加工条件：	注射成型 Injection Molding	挤出 Extrusion

技术参数

物理性能
PHYSICAL Ultramid® A3L BK7793 Vydyne® 67B 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：23℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：23℃，2.0 mm)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL Ultramid® A3L BK7793 Vydyne® 67B 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2

泊松比
Poisson's ratio ISO 527-2

冲击性能
IMPACT Ultramid® A3L BK7793 Vydyne® 67B 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultramid® A3L BK7793 Vydyne® 67B 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD：23~55℃，2 mm)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃，2 mm)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

加工方式

注射 Ultramid® A3L BK7793 Vydyne® 67B 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

螺杆压缩比

螺杆转速 rpm

挤出 Ultramid® A3L BK7793 Vydyne® 67B 单位测试方法

口模温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
挤出
备注
返回顶部

PA66，Ultramid® A3L BK7793对比PA66，Vydyne® 67B对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别