HCPP，Hanwha Total PP BI300对比HCPP，Borpact™ BC918CF物性表,价格行情_搜料

牌号信息	Hanwha Total PP BI300 物性表 HCPP & 韩国韩华指导价格：暂无塑料库存：缺货	Borpact™ BC918CF 物性表 HCPP & 奥地利北欧化工指导价格：暂无塑料库存：缺货
牌号简介	Bi300是一种结晶度较高的高等规嵌段共聚物，与普通聚丙烯相比，由于其结晶性好，橡胶设计最佳，因此在高硬度和冲击强度之间具有良好的性能平衡。由该等级制成的薄膜具有很高的耐热性和优越的机械强度，因此该等级非常适合于干馏袋薄膜的应用。 Description BI300 is a high isotactic Block Copolymer which has higher crystallinity, compared to general PP. Due to high crystalline nature & optimum rubber design, BI300 has an excellent property balance between high stiffness and impact strength. Films made from this grade provide high heat resistance and superior mechanical strength, thus this grade is highly suited to retort pouch film application. Characteristics Good balance physical property between stiffness & impact strength Punch resistance Heat resistance High transparency Applications Retort pouch, Cast film	BC918CF是一种异相共聚物。BC918CF是一种高结晶共聚薄膜树脂。该等级适用于在铸造生产线上生产无取向薄膜、采用空气冷却的传统吹塑薄膜生产线以及热成型薄膜/片材的辊叠工艺。CAS号9010-79-1 BC918CF is a heterophasic copolymer. BC918CF is a high crystalline copolymer film resin. This grade is suitable for the manufacturing of unoriented films on cast lines, conventional blown film lines with air cooling as well as roll stack process for thermoformable films/sheets. CAS-No. 9010-79-1

产品描述
厂家：	韩国韩华 HANWHA	奥地利北欧化工 Borealis AG
类别：	HCPP HC PP	HCPP HC PP
填料：
用途：	医疗/护理用品,薄膜,食品包装	薄膜,层压板,无取向薄膜,食品包装,标签,流延薄膜,支架托盘
性能特点：	机械强度好,表面光泽度好,冲击性能好,尺寸稳定性好,易消毒,结晶,耐高温,嵌段共聚物,耐低温冲击,耐高压加热性 Good Rigidity,Good surface appearance,High impact resistance,Good Dimensional Stability,Good disinfection,Crystal,High Heat Resistance,Block Copolymer,low-temperature impact resistance,High pressure heat resistance	机械强度好,透光性好,韧性好,高纯度,结晶,机械强度好-撕裂,共聚物,耐低温冲击 Good Rigidity,Good Clarity,Good flexibility,High purity,Crystal,Good tear strength,Copolymer,low-temperature impact resistance
加工条件：	注射成型 Injection Molding	吹塑薄膜

技术参数

物理性能
PHYSICAL Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

薄膜
Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂，50 µm)
Tensile strain % ISO 527-3

拉伸应变(MD，断裂，60 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，50 µm)
Tensile strain % ISO 527-3

拉伸应变(TD，断裂，60 µm)
Tensile strain % ASTM D882

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(MD，屈服，60 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，60 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，60 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，60 µm)
tensile strength MPa ASTM D882

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量(MD，50 µm)
Tensile modulus MPa ISO 527-3

拉伸模量(TD，50 µm)
Tensile modulus MPa ISO 527-3

薄膜厚度(测试)
film thickness µm

冲击性能
IMPACT Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(5℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(-20℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 3

光学性能
OPTICAL Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

光泽度(20°，50 µm)
gloss ASTM D2457

雾度(50 µm)
Haze % ASTM D1003

雾度(60 µm)
Haze % ASTM D1003

机械性能
MECHANICAL Hanwha Total PP BI300 Borpact™ BC918CF 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(23℃，注塑成型)
Bending modulus MPa ISO 178

洛氏硬度(R 级)
Rockwell hardness ASTM D785

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 压力1 (10N)

1 一般属性：这些不能被视为规格。

2 0.079 in/min