LDPE，Lupolen 1800 U对比LDPE，SABIC® LDPE 1965N0物性表,价格行情_搜料

牌号信息	Lupolen 1800 U 物性表 LDPE & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货	SABIC® LDPE 1965N0 物性表 LDPE & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lupolen 1800 U是一种低密度聚乙烯（LDPE）树脂，用于各种加工方法，如注射成型和复合。它具有很高的流动性和很好的软韧性、尺寸稳定性和良好的加工平衡。Lupolen 1800 U以颗粒形式交付，未添加。它被广泛应用于注塑成型，如薄壁包装（twim）和家庭用品。Lupolen 1800 U也用于颜色和添加剂批次的配制领域，并用作粘度改进剂。客户报告说，Lupolen 1800 U的高熔体流动速率（MFR）使颜料和添加剂能够在高负荷下很好地分散和均匀化。Lupolen 1800 U不适用于医药应用。 Lupolen 1800 U is a low density polyethylene (LDPE) resin used in various processing methods such as injection molding and compounding. It exhibits very high flowability and a very good balance of softness and toughness, dimensional stability and good processing. Lupolen 1800 U is delivered in pellet form and is not additivated. It is used in a wide range of injection molding applications such as thin-wall packaging (TWIM) and housewares. Lupolen 1800 U is also used in the area of compounding for color and additive batches and as a viscosity modifier. Customers have reported that the high melt flow rate (MFR) of Lupolen 1800 U enables very good dispersion and homogenization at high loads with pigments and additives. Lupolen 1800 U is not intended for use in medical and pharmaceutical applications.	SABIC® LDPE 1965N0是一种快速流动的聚合物，适用于机械性能不重要的柔性物品。这种材料通常不易弯曲。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® LDPE 1965N0 is a fast flowing polymer for flexible articles where mechanical properties are not critical. The material has a typically low tendency to warp. This product is not intended for and must not be used in any pharmaceutical/medical applications.

产品描述
厂家：	荷兰利安德巴塞尔 LyondellBasell	沙特沙伯基础 SABIC
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	玩具,包装,塑料改性,家用货品,护罩,色母料,薄壁包装,体育用品,外壳	母料
性能特点：	易加工,韧性好,尺寸稳定性好,流动性高,易流动,成型周期快,耐低温柔性,低密度,着色性好 Excellent Processability,Good flexibility,Good Dimensional Stability,High liquidity,Good liquidity,Quick molding cycle,Low temperature toughness,Low density,Good coloring	低翘曲性,韧性好,流动性高,低密度 Low warping,Good flexibility,High liquidity,Low density
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Lupolen 1800 U SABIC® LDPE 1965N0 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(190℃，5 kg)
Melt Volume Rate cm³/10min

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(190℃，5.0kg)
Melt Flow Rate g/10min

螺旋流动长度
Spiral flow length cm 内部方法

热性能
THERMAL Lupolen 1800 U SABIC® LDPE 1965N0 单位
UNIT 测试方法
TEST METHOD

Enthalpy Change
Enthalpy Change J/g DIN 53765

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ DIN 53765

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

机械性能
MECHANICAL Lupolen 1800 U SABIC® LDPE 1965N0 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，2 mm，模压成型)
Tensile strain % ISO 527-2/1BA/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服，2 mm，模压成型)
tensile strength MPa

拉伸强度(断裂，2 mm，模压成型)
tensile strength MPa

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(2 mm，模压成型)
Tensile modulus MPa ISO 527-2/1BA/50

拉伸蠕变模量(1 hr)
Tensile creep modulus MPa

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，模压成型)
Shore hardness ISO 868

冲击性能
IMPACT Lupolen 1800 U SABIC® LDPE 1965N0 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃，模压成型)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃，模压成型)
Impact strength of cantilever beam notch kJ/m²

加工方式

注射 Lupolen 1800 U SABIC® LDPE 1965N0 单位测试方法

加工熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 熔体温度: 356°F, 注塑压力: 1.45E+4 psi

3 2 mm

4 Tested in 10% nonionic surfactants

1 一般属性：这些不能被视为规格。

2 4mm