技术参数
物理性能 PHYSICAL
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
密度
Density
g/cm³
ASTM D297
弹性体 ELASTOMER
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
压缩形变(149℃,70 hr)
Compression deformation
%
ASTM D395
压缩形变(175℃,166 hr)
Compression deformation
%
ASTM D395
压缩形变(200℃,22 hr)
Compression deformation
%
ASTM D395
压缩形变(200℃,22 hr)
Compression deformation
%
ASTM D395B
压缩形变(200℃,70 hr)
Compression deformation
%
ASTM D395
压缩形变(232℃,70 hr)
Compression deformation
%
ASTM D395
压缩形变(23℃,70 hr)
Compression deformation
%
ASTM D395
压缩形变(242℃,70 hr)
Compression deformation
%
ASTM D395
压缩形变(288℃,70 hr)
Compression deformation
%
ASTM D395
拉伸应变(断裂)
Tensile strain
%
ASTM D1414
拉伸应变(断裂)
Tensile strain
%
ASTM D412
拉伸强度(100% 应变)
tensile strength
MPa
ASTM D1414
拉伸强度(100% 应变)
tensile strength
MPa
ASTM D412
拉伸强度(50% 应变)
tensile strength
MPa
ASTM D1414
拉伸强度(断裂)
tensile strength
MPa
ASTM D1414
拉伸强度(断裂)
tensile strength
MPa
ASTM D412
撕裂强度
tear strength
kN/m
ASTM D624
老化性能 AGING
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
体积变化(135℃,70 hr,在 Ford ATF 中)
Volume change
%
ASTM D471
体积变化(135℃,70 hr,在 MIL-H-5606 中)
Volume change
%
ASTM D471
体积变化(135℃,70 hr,在 Wagner 21B 中)
Volume change
%
ASTM D471
体积变化(175℃,70 hr,在Stauffer 7700 液体中)
Volume change
%
ASTM D471
体积变化(200℃,1000 hr,在 Castrol 325 中)
Volume change
%
ASTM D471
体积变化(240℃,100 hr,在 Castrol 325 中)
Volume change
%
ASTM D471
体积变化(242℃,70 hr,在蒸汽中)
Volume change
%
ASTM D471
拉伸强度的变化率(135℃,70 hr,在 Ford ATF 中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(135℃,70 hr,在 MIL-H-5606 中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(135℃,70 hr,在 Wagner 21B 中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(175℃,70 hr,在Stauffer 7700 液体中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(200℃,1000 hr,在 Castrol 325 中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(240℃,100 hr,在 Castrol 325 中)
The rate of change in tensile strength
%
ASTM D471
拉伸强度的变化率(242℃,70 hr,在蒸汽中)
The rate of change in tensile strength
%
ASTM D471
极限伸长率的变化率(135℃,70 hr,在 Ford ATF 中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(135℃,70 hr,在 MIL-H-5606 中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(135℃,70 hr,在 Wagner 21B 中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(175℃,70 hr,在Stauffer 7700 液体中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(200℃,1000 hr,在 Castrol 325 中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(240℃,100 hr,在 Castrol 325 中)
Change rate of ultimate elongation
%
ASTM D471
极限伸长率的变化率(242℃,70 hr,在蒸汽中)
Change rate of ultimate elongation
%
ASTM D471
空气中拉伸强度的变化率(149℃,70 hr)
The rate of change in tensile strength in air
%
ASTM D573
空气中拉伸强度的变化率(232℃,70 hr)
The rate of change in tensile strength in air
%
ASTM D573
空气中拉伸强度的变化率(276℃,70 hr)
The rate of change in tensile strength in air
%
ASTM D573
空气中拉伸强度的变化率(288℃,70 hr)
The rate of change in tensile strength in air
%
ASTM D573
空气中极限伸长率的变化率(149℃,70 hr)
The rate of change in ultimate elongation in air
%
ASTM D573
空气中极限伸长率的变化率(232℃,70 hr)
The rate of change in ultimate elongation in air
%
ASTM D573
空气中极限伸长率的变化率(276℃,70 hr)
The rate of change in ultimate elongation in air
%
ASTM D573
空气中极限伸长率的变化率(288℃,70 hr)
The rate of change in ultimate elongation in air
%
ASTM D573
空气中硬度计硬度的变化率(149℃,70 hr)
The rate of change in hardness of a hardness tester in the air
ASTM D573
空气中硬度计硬度的变化率(232℃,70 hr)
The rate of change in hardness of a hardness tester in the air
ASTM D573
空气中硬度计硬度的变化率(276℃,70 hr)
The rate of change in hardness of a hardness tester in the air
ASTM D573
空气中硬度计硬度的变化率(288℃,70 hr)
The rate of change in hardness of a hardness tester in the air
ASTM D573
邵氏硬度的变化率(135℃,70 hr,在 Ford ATF 中)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(135℃,70 hr,在 MIL-H-5606 中)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(135℃,70 hr,在 Wagner 21B 中)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(175℃,70 hr,在Stauffer 7700 液体中)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(191℃,70 hr,在 Ford ATF 中)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(200℃,1000 hr,in Castrol 325)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(240℃,100 hr,in Castrol 325)
The rate of change in Shore hardness
ASTM D471
邵氏硬度的变化率(242℃,70 hr,in Steam)
The rate of change in Shore hardness
ASTM D471
热性能 THERMAL
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
使用温度
Operating temperature
℃
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
1/℃
ASTM E228
补充信息
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
Rubber Classification
Rubber Classification
ASTM D1418
TR 10/50
TR 10/50
℃
ASTM D1329
机械性能 MECHANICAL
Fluoraz FEPM 797
Fluoraz FEPM 799
单位 UNIT
测试方法 TEST METHOD
摩擦系数(与自身 - 动态)
friction coefficient
ASTM D1894
摩擦系数(与自身 - 静态)
friction coefficient
ASTM D1894
洛氏硬度(M 级)
Rockwell hardness
ASTM D785
邵氏硬度(邵氏 A)
Shore hardness
ASTM D2240