牌号信息	YUCLAIR® FN810 物性表 LLDPE & 韩国SK化学指导价格：暂无塑料库存：缺货	YUCLAIR® FN812 物性表 LLDPE & 韩国SK化学指导价格：暂无塑料库存：缺货
牌号简介	YUCLAIR® FN810是专为拉伸包装膜应用而设计的辛烯-1共聚物。YUCLAIR® FN810提供比竞争性LLDPE胶片等级更坚固的胶片。因此，YUCLAIR® FN810表现出优异的抗拉强度、撕裂强度、无凝胶、粘结性能。高清晰度和良好的加工性能使该树脂与传统低密度聚乙烯（LDPE）混合后成为薄膜应用的理想选择。YUCLAIR® FN810可以使用标准挤压技术很容易地加工成吹塑薄膜。YUCLAIR® FN810符合21 CFR177.1520中所有食品接触的FDA法规。 YUCLAIR FN810 is octene-1 copolymer designed for use in stretch wrap film application. YUCLAIR FN810 provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FN810 shows superior tensile strength, tear strength, gel-free, cling property. Outstanding clarity and good processibility make this resin an ideal choice for film application when blended with conventional LDPE. YUCLAIR FN810 can be processed readily into blown film using standard extrusion techniques. YUCLAIR FN810 complies with FDA regulations in 21 CFR177.1520 for all food contact.	YUCLAIR® FN812是一种辛烯-1共聚物，设计用于干层压薄膜应用。YUCLAIR® FN812提供比竞争性LLDPE胶片等级更坚固的胶片。因此，YUCLAIR® FN812表现出优异的抗拉强度、撕裂强度、无凝胶、抗块和密封性。YUCLAIR® FN812含有最佳的添加剂，因此是理想的LLDPE树脂层压膜。YUCLAIR® FN812可以使用标准挤压技术很容易地加工成吹塑薄膜。YUCLAIR® FN812符合21 CFR177.1520中所有食品接触的FDA法规。 YUCLAIR FN812 is octene-1 copolymer designed for use in dry lamination film application. YUCLAIR FN812 provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FN812 shows superior tensile strength, tear strength, gel-free, antiblock and sealibility. YUCLAIR FN812 contains optimum of additives and is thus ideally suitable as a LLDPE resin for lamination film. YUCLAIR FN812 can be processed readily into blown film using standard extrusion techniques. YUCLAIR FN812 complies with FDA regulations in 21 CFR177.1520 for all food contact.

产品描述
厂家：	韩国SK化学 SKC	韩国SK化学 SKC
类别：	LLDPE Linear low density polyethylene	LLDPE Linear low density polyethylene
填料：
用途：	工业应用,混合,薄膜,拉伸缠绕	薄膜,工业应用,包装,层压板
性能特点：	易加工,透光性好,食品接触,拉伸性能好,机械强度好-撕裂,高粘接度,辛烯共聚单体,共聚物 Excellent Processability,Good Clarity,Food contact compliance,Good Tensile Strength,Good tear strength,High adhesion degrees,Octene copolymer,Copolymer	高光滑性,抗结块性,食品接触,拉伸性能好,机械强度好-撕裂,辛烯共聚单体,共聚物 Smoothness,High anti-blocking,Food contact compliance,Good Tensile Strength,Good tear strength,Octene copolymer,Copolymer
加工条件：	吹塑薄膜	挤出 Extrusion

技术参数

物理性能
PHYSICAL YUCLAIR® FN810 YUCLAIR® FN812 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
YUCLAIR® FN810 YUCLAIR® FN812 单位
UNIT 测试方法
TEST METHOD

Spencer Impact
Spencer Impact J ASTM D3420

拉伸应变(MD，断裂)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，50 µm)
tensile strength MPa ASTM D882

薄膜厚度(测试)
film thickness µm ASTM D746

热性能
THERMAL YUCLAIR® FN810 YUCLAIR® FN812 单位
UNIT 测试方法
TEST METHOD

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

脆化温度
Embrittlement temperature ℃ ASTM D746

光学性能
OPTICAL YUCLAIR® FN810 YUCLAIR® FN812 单位
UNIT 测试方法
TEST METHOD

雾度
Haze % ASTM D1003

雾度(50 µm)
Haze % ASTM D1003

补充信息
YUCLAIR® FN810 YUCLAIR® FN812 单位
UNIT 测试方法
TEST METHOD

撕裂强度(MD)
tear strength kN/m ASTM D1922

撕裂强度(TD)
tear strength kN/m ASTM D1922

加工方式

挤出 YUCLAIR® FN810 YUCLAIR® FN812 单位测试方法

口模温度 °C

料筒1区温度 °C

料筒3区温度 °C

料筒5区温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
光学性能
补充信息
加工方式
挤出
备注
返回顶部

LLDPE，YUCLAIR® FN810对比LLDPE，YUCLAIR® FN812对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别