PA12弹性体，Pebax® Rnew 35R53 SP 01对比PA12弹性体，Pebax® Rnew 40R53 SP 01物性表,价格行情_搜料

牌号信息	Pebax® Rnew 35R53 SP 01 物性表 PA12弹性体 & 法国阿科玛指导价格：暂无塑料库存：缺货	Pebax® Rnew 40R53 SP 01 物性表 PA12弹性体 & 法国阿科玛指导价格：暂无塑料库存：缺货
牌号简介	聚醚嵌段酰胺Pebax® Rnew 35R53 SP 01是一种以可再生资源为基础，由柔性聚醚和刚性聚酰胺制成的热塑性弹性体。该SP等级已发展为耐热和抗紫外线。 Polyether block Pebax® Rnew® 35R53 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. The percentage of renewable carbon according to ASTM D 6866 is 28-32%.	聚醚嵌段酰胺Pebax® Rnew 40R53 SP 01是一种以可再生资源为基础，由柔性聚醚和刚性聚酰胺制成的热塑性弹性体。该SP等级已发展为耐热和抗紫外线。 Polyether block Pebax® Rnew® 40R53 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. The percentage of renewable carbon according to ASTM D 6866 is 44-48%

产品描述
厂家：	法国阿科玛 Arkema	法国阿科玛 Arkema
类别：	PA12弹性体 PA12弹性体	PA12弹性体 PA12弹性体
填料：
用途：
性能特点：	耐候抗UV,可回收,耐高温 Weather resistance is good,Renewable resources,High Heat Resistance	耐候抗UV,可回收,耐高温 Weather resistance is good,Renewable resources,High Heat Resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate %

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：4.0 mm，24 hrs)
Shrinkage rate %

收缩率(MD：4.0 mm，24 hrs)
Shrinkage rate % 内部方法

收缩率(TD：4.0 mm，24 hrs)
Shrinkage rate %

收缩率(TD：4.0 mm，24 hrs)
Shrinkage rate % 内部方法

冲击性能
IMPACT Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength ISO 179

热性能
THERMAL Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ ISO 11357-3

维卡软化温度
Vicat Softening Temp ℃ ISO 306

补充信息
Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位
UNIT 测试方法
TEST METHOD

Renewable Carbon Conent
Renewable Carbon Conent % ASTM D6866

机械性能
MECHANICAL Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 D)
Shore hardness

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，15 秒)
Shore hardness

邵氏硬度(邵氏 D，15 秒)
Shore hardness ISO 868

加工方式

注射 Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

挤出 Pebax® Rnew 35R53 SP 01 Pebax® Rnew 40R53 SP 01 单位测试方法

干燥时间 hr

干燥温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Mold at 20°C

3 Samples conditioned 15 days at 23°C - 50 % R.H

1 一般属性：这些不能被视为规格。

2 Mold at 20°C

3 Samples conditioned 15 days at 23°C - 50 % R.H


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
补充信息
机械性能
加工方式
注射
挤出
备注
返回顶部