PEEK，SCHULATEC® PEEK NV 12对比PEEK，KetaSpire® KT-880P物性表,价格行情_搜料

牌号信息	SCHULATEC® PEEK NV 12 物性表 PEEK & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货	KetaSpire® KT-880P 物性表 PEEK & 比利时索尔维指导价格：暂无塑料库存：缺货
牌号简介	无增强聚乙烯醚酮，低粘度 unreinforced polyetheretherketone, low viscosity	KetaSpire® KT-880P是一种高流动等级的无增强聚醚醚酮（PEEK），以天然色粗粉形式提供。KetaSpire Peek是按照最高的行业标准生产的，具有独特的性能组合，包括优异的耐磨性、一流的抗疲劳性、易熔加工性、高纯度和对有机物、酸和碱具有优异的耐化学性。这些特性使其非常适合用于医疗、运输、电子、化学加工和其他工业用途。KetaSpire® KT-880P用于挤压复合。这种粉末也可作为KT-880NT在自然色颗粒形式注射成型。 KetaSpire® KT-880P is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. KetaSpire® KT-880P is intended for extrusion compounding. This powder is also available as KT-880NT in a natural-color pellet form for injection molding.

产品描述
厂家：	荷兰利安德巴塞尔 LyondellBasell	比利时索尔维 Solvay
类别：	PEEK	PEEK PEEK
填料：
用途：		半导体模制化合物,电气/电子应用领域,工业应用
性能特点：		冲击性能好,尺寸稳定性好,流动性高,机械强度好-延展,阻燃,耐高温,耐疲劳性好,耐化学性 High impact resistance,Good Dimensional Stability,High liquidity,Ductility,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance
加工条件：	注射成型,挤出 Injection Molding,Extrusion	压缩模塑

技术参数

物理性能
PHYSICAL SCHULATEC® PEEK NV 12 KetaSpire® KT-880P 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

熔体质量流动速率(400℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL SCHULATEC® PEEK NV 12 KetaSpire® KT-880P 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2/1A/50

冲击性能
IMPACT SCHULATEC® PEEK NV 12 KetaSpire® KT-880P 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam ASTM D256

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam ISO 180

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

热性能
THERMAL SCHULATEC® PEEK NV 12 KetaSpire® KT-880P 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ ASTM D3417

玻璃化转变温度
Glass transition temperature ℃ ASTM D3417

线性热膨胀系数(MD：-50~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

加工方式

注射 SCHULATEC® PEEK NV 12 KetaSpire® KT-880P 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Measured on annealed samples 3,2 mm thick, 200°C/2h

1 一般属性：这些不能被视为规格。

2 结晶

3 淬火


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注