LDPE，PAXOTHENE® NA207-66对比LDPE，SUMIKATHENE® L718-H物性表,价格行情_搜料

牌号信息	PAXOTHENE® NA207-66 物性表 LDPE & 台湾台聚指导价格：暂无塑料库存：缺货	SUMIKATHENE® L718-H 物性表 LDPE & 日本住友指导价格：暂无塑料库存：缺货
牌号简介	PAXOTHENE® NA207-66（LDPE）是一种低密度聚乙烯树脂，具有较高的熔融指数，特别适用于注塑和挤出成型。PAXOTHENE® NA207-66具有良好的流动性，适用于厚度为0.010~0.040mm的薄膜或袋。上述包装袋适用于西服、面包、水果、蔬菜、鱼、肉和杂货的包装。PAXOTHENE® NA207-66具有良好的防滑和防堵剂配方，由所述树脂制成的袋子易于打开，具有出色的光泽。这使得商品对顾客更具吸引力。PAXOTHENE® NA207-66也可以注塑成各种零件，如塑料树干，玩具和文具的小零件。 PAXOTHENE NA207-66 (LDPE) is a low density polyethylene resin with high melt index especially suitable for injection & extrusion molding. Owing to its excellent flowability, PAXOTHENE NA207-66 is suitable for films or bags with thickness of 0.010~0.040 mm. The said bags are for package of suit, bakery, fruit, vegetable, fish, meat, and grocery. PAXOTHENE NA207-66 is well formulated with slip and anti-block agents, bags made from said resin are easy to open and with outstanding gloss. This makes goods more attractive to customers. PAXOTHENE NA207-66 also could be injection molded into various parts, such as trunk of plastic trees, small parts for toy and stationery.	SUMIKATHENE® L718-H是一种低密度聚乙烯材料,。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:挤出。 SUMIKATHENE® L718-H的主要特性有: 快速成型周期无气味/无味道 SUMIKATHENE® L718-H的典型应用领域为:涂覆应用 SUMIKATHENE® L718-H是一种低密度聚乙烯材料,。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:挤出。 SUMIKATHENE® L718-H的主要特性有: 快速成型周期无气味/无味道 SUMIKATHENE® L718-H的典型应用领域为:涂覆应用

产品描述
厂家：	台湾台聚 USI	日本住友 Sumitomo
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	袋子,食品包装,薄膜,玩具	层压板
性能特点：	表面光泽度好,高光滑性,易流动,抗结块性,食品接触,低密度 Good surface appearance,Smoothness,Good liquidity,High anti-blocking,Food contact compliance,Low density	成型周期快,低VOC Quick molding cycle,Low odor
加工条件：	薄膜挤出 Film extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ JIS K6922-1

抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体质量流动速率
Melt Flow Rate g/10min JIS K6922-1

熔体质量流动速率()
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位
UNIT 测试方法
TEST METHOD

弯曲模量(23℃)
Bending modulus MPa ASTM D747

拉伸应变(断裂)
Tensile strain % 内部方法

拉伸强度(断裂)
tensile strength MPa 内部方法

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D)
Shore hardness JIS K7215

冲击性能
IMPACT PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位
UNIT 测试方法
TEST METHOD

拉伸冲击强度
Tensile impact strength kJ/m² ASTM D1822

热性能
THERMAL PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ DSC

维卡软化温度
Vicat Softening Temp ℃ JIS K7206

加工方式

注射 PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位测试方法

喷嘴温度 °C

干燥时间 Hr

干燥温度 °C

建议水份含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

挤出成型条件 PAXOTHENE® NA207-66 SUMIKATHENE® L718-H 单位测试方法

干燥时间 Hr

干燥温度 °C

建议水份含量 %

模头温度 °C

第一区温度 °C

第三区温度 °C

第二区温度 °C

第五区温度 °C

第四区温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
挤出成型条件
备注
返回顶部

LDPE，PAXOTHENE® NA207-66对比LDPE，SUMIKATHENE® L718-H对比物性表,价格行情_搜料_soliao