PA66，LNP™ LUBRICOMP™ RFN16SXZ compound对比PA66，LNP™ LUBRICOMP™ RFP36L compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ RFN16SXZ compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ RFP36L compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP LubricompRFN16SXZ是一种基于尼龙66树脂的化合物，含有30%玻璃纤维、5%MoS2。这种材料的附加特性包括：热稳定，耐磨。也称为：lnplubricomp化合物rfl-4216 hs产品再订购名称：rfn16sxz LNP LUBRICOMP RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4216 HS Product reorder name: RFN16SXZ	Zythane 5050D是一种基于聚酯的TPU，专门为挤压应用而设计。它具有优异的耐磨性和韧性，具有良好的水解稳定性、耐油性、耐燃油性和耐溶剂性。它是以未着色的颗粒形式提供的。典型应用：Zythane 5050D应用包括螺旋和气动管道、圆形和V形带、吹塑波纹管。 Zythane 5050D is a polyester--based TPU specifically formulated for extrusion applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 5050D applications include among others spiral and pneumatic tubing, round and V belting, blow molded bellows.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 30	玻璃纤维 30
用途：		管件
性能特点：	润滑性,耐磨,热稳定性好 Lubricating,Good wear resistance,Heat Stabilized	韧性好,耐水解,耐磨,耐油,耐化学性,耐燃油 Good flexibility,Hydrolysis stability,Good wear resistance,Grease resistance,Solvent resistance,Fuel resistance
加工条件：	注射成型 Injection Molding	挤出 Extrusion

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ RFN16SXZ compound LNP™ LUBRICOMP™ RFP36L compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % 内部方法

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ RFN16SXZ compound LNP™ LUBRICOMP™ RFP36L compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

摩擦系数(与自身 - 动态)
friction coefficient

摩擦系数(与自身 - 静态)
friction coefficient

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ RFN16SXZ compound LNP™ LUBRICOMP™ RFP36L compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ RFN16SXZ compound LNP™ LUBRICOMP™ RFP36L compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

加工方式

注射 LNP™ LUBRICOMP™ RFN16SXZ compound LNP™ LUBRICOMP™ RFP36L compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 C 模具


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

PA66，LNP™ LUBRICOMP™ RFN16SXZ compound对比PA66，LNP™ LUBRICOMP™ RFP36L compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别