牌号信息	ARLEN™ C240N 物性表 PA6T & 日本三井指导价格：暂无塑料库存：缺货	ARLEN™ C240 物性表 PA6T & 日本三井指导价格：暂无塑料库存：缺货
牌号简介	ARLEN™ C240N是一种聚酰胺 6T（尼龙 6T）材料,含有的填充物为40% 玻璃纤维增强材料。该产品在北美洲有供货,。 ARLEN™ C240N的主要特性有: 阻燃/额定火焰 Flame Retardant ARLEN™ C240N的典型应用领域为:电气/电子应用 ARLEN™ C240N is a Polyamide 6T (Nylon 6T) material filled with 40% glass fiber. It is available in North America. Important attributes of ARLEN™ C240N are: Flame Rated Flame Retardant Typical application of ARLEN™ C240N: Electrical/Electronic Applications	ARLEN™ C240是一种聚酰胺 6T（尼龙 6T）材料,含有的填充物为40% 玻璃纤维增强材料。该产品在北美洲有供货,。 ARLEN™ C240的主要特性为:阻燃/额定火焰。 ARLEN™ C240的典型应用领域为:电气/电子应用 ARLEN™ C240 (Dry) ARLEN™ C240 is a Polyamide 6T (Nylon 6T) material filled with 40% glass fiber. It is available in North America. Primary attribute of ARLEN™ C240: Flame Rated. Typical application of ARLEN™ C240: Electrical/Electronic Applications ARLEN™ C240 ARLEN™ C240 by Mitsui Chemicals is a modified polyamide 6T reinforced with 40% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ C240 is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 HB flame rating. Features: High dimensional stability High melting point High rigidity Minimum water absorption Good chemical and heat resistance Applications: Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.

产品描述
厂家：	日本三井 Mitsui	日本三井 Mitsui
类别：	PA6T PA 6T	PA6T PA 6T
填料：	玻璃纤维 40	玻璃纤维 40
用途：	电气/电子应用领域	电气/电子应用领域
性能特点：	阻燃,防火阻燃等级V-0 Flame Characteristics,V-0	防火阻燃等级HB HB
加工条件：

技术参数

物理性能
PHYSICAL ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

吸水率 Water Absorption(100℃，24hr)
Water Absorption % ASTM D570

吸水率 Water Absorption(23℃，24hr)
Water Absorption % ASTM D570

吸水率(100℃，24hr)
Water absorption rate % ASTM D570

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度 Density
Density g/cm³ ASTM D792

收缩率 Shrinkage(MD：2.0 mm)
Shrinkage rate % ASTM D955

收缩率 Shrinkage(TD：2.0 mm)
Shrinkage rate % ASTM D955

收缩率(MD：2.0 mm)
Shrinkage rate % ASTM D955

收缩率(TD：2.0 mm)
Shrinkage rate % ASTM D955

冲击性能
IMPACT ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度 Izod Notched Impact strength
Izod Notched Impact strength J/m ASTM D256

热性能
THERMAL ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

热变形温度 HDT(1.8 MPa，未退火)
Hot deformation temperature HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃

熔融温度 Melting temperature
Melting temperature ℃

玻璃化转变温度
Glass transition temperature ℃ DSC

玻璃化转变温度 Glass Transition Temperature
Glass Transition Temperature ℃ DSC

线性热膨胀系数 Coeff.of linear therm expansion(MD)
Coeff. of linear thermal expansion 1/℃ ASTM D696

线性热膨胀系数 Coeff.of linear therm expansion(TD)
Coeff. of linear thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

介电常数 Dielectric Constant(1 MHz)
Dielectric Constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

介电强度 Dielectric Strength
Dielectric Strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率 Volume Resistivity
Volume Resistance ohms·cm ASTM D257

耗散因数 Dissipation Factor(1 MHz)
Dissipation Factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级 Flame Class Rating
Flame Class Rating UL 94

机械性能
MECHANICAL ARLEN™ C240N ARLEN™ C240 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度 Flexural Strength
Flexural Strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量 Flexural Modulus
Flexural Modulus MPa ASTM D790

拉伸应变 Tensile Strain(断裂 brk)
Tensile Strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度 Tensile Strength
Tensile Strength MPa ASTM D638

洛氏硬度 Rockwell Hardness(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ASTM D785

加工方式

注射 ARLEN™ C240N ARLEN™ C240 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

螺杆转速 rpm

注塑成型 Injection Molding ARLEN™ C240N ARLEN™ C240 单位测试方法

中段温度 Middle Temperature -Zone 2 °C

前段温度 Front Temperature -Zone 3 °C

后段温度 Rear Temperature -Zone 1 °C

喷嘴温度 Nozzle Temperature °C

干燥时间 Drying Time hr

干燥温度 Drying Temperature °C

料斗温度 Hopper Temperature °C

模具温度 Mold Temperature °C

注射速度 Injection speed

螺杆转速 Screw Speed rpm

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
注塑成型 Injection Molding
备注
返回顶部

PA6T，ARLEN™ C240N对比PA6T，ARLEN™ C240对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别