PP，HiPrene® HT42WGT对比PP，HiPrene® MT42物性表,价格行情_搜料

牌号信息	HiPrene® HT42WGT 物性表 PP & 韩国加德士指导价格：暂无塑料库存：缺货	HiPrene® MT42 物性表 PP & 韩国加德士指导价格：暂无塑料库存：缺货
牌号简介	HiPrene® HT42WGT是一种20%的矿物填充聚丙烯化合物，适用于注塑成型。这种材料具有良好的流动性和良好的平衡力学性能。该等级可采用天然或颜色匹配的颗粒形式。 HiPrene® HT42WGT is a 20% mineral filled polypropylene compound suitable for injection moulding. This material has a good flowability and excellent balanced mechanical properties. This grade is available in natural or color-matched, pellet form.	HiPrene® MT42是一种中等熔融流动、20%矿物填充的聚丙烯化合物。这种材料流动性好，易于加工。由于其良好的冲击/刚度平衡适用于工业零件和不可见的汽车内饰零件。该等级可采用天然或颜色匹配的颗粒形状。 HiPrene® MT42 is a medium melt flow, 20% mineral filled polypropylene compound. This material has good flowability and it is easy to process. Because of it's good impact/stiffness balance is suitable for Industrial Parts and non-visible automotive interior parts.This grade is available in natural or color-matched, pellet form.

产品描述
厂家：	韩国加德士 GS Caltex	韩国加德士 GS Caltex
类别：	PP PP not specified	PP PP not specified
填料：	矿物 20	矿物 20
用途：	汽车领域的应用,大型家用电器和小型家用电器	工业应用,汽车领域的应用
性能特点：	机械强度好,易加工,易流动,收缩性低,耐高温 Good Rigidity,Excellent Processability,Good liquidity,Low contractility,High Heat Resistance	冲击性能好,流动性中等,易加工,机械强度好 High impact resistance,Moderate liquidity,Excellent Processability,Good Rigidity
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL HiPrene® HT42WGT HiPrene® MT42 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

挥发物
Volatiles % 内部方法

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(TD)
Shrinkage rate % 内部方法

比重 Specific Gravity ()
g/cm³ ASTM D792

灰份含量(600℃)
Ash Content % ISO 3451

熔体质量流动速率
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率 Melt Flow Rate(2.16Kg，230℃)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT HiPrene® HT42WGT HiPrene® MT42 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度 Izod Notched Impact strength(-10℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度 Izod Notched Impact strength(23℃)
Izod Notched Impact strength J/m ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

机械性能
MECHANICAL HiPrene® HT42WGT HiPrene® MT42 单位
UNIT 测试方法
TEST METHOD

弯曲强度 Flexural strength
Flexural strength MPa ASTM D790

弯曲模量 Flexural Modulus
Flexural Modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸伸长率 Tensile Elongation
Tensile Elongation % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度 Tensile strength(屈服 yld)
Tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

洛氏硬度 Rockwell Hardness
Rockwell hardness R Scale ASTM D-785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

热性能
THERMAL HiPrene® HT42WGT HiPrene® MT42 单位
UNIT 测试方法
TEST METHOD

热变形温度 HDT(0.45 MPa)
Hot deformation temperature HDT ℃ ASTM D648

加工方式

注射 HiPrene® HT42WGT HiPrene® MT42 单位测试方法

保压 MPa

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料斗温度 °C

模具温度 °C

注塑 Injection HiPrene® HT42WGT HiPrene® MT42 单位测试方法

中段温度 Middle Temperature ℃

保持压力 Holding Pressure bar

前段温度 Front Temperature ℃

后段温度 Rear Temperature ℃

喷嘴温度 Nozzle Temperature ℃

模具温度 Mold Temperature ℃

注射压力 Injection pressure bar

注射速度 Injection speed

熔融温度 Melt Temperature ℃

背压 Back Pressure bar

螺杆转速 Screw speed

进料温度 Feeding temperature ℃

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

1 一般属性：这些不能被视为规格。

2 0.079 in/min