PA6，LNP™ THERMOCOMP™ PF003 compound对比PA6，Durethan® BKV15 000000 DUS008物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ PF003 compound 物性表 PA6 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Durethan® BKV15 000000 DUS008 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	lnp thermocomp pf003化合物lnp thermocomppf003是一种基于尼龙6树脂的化合物，含有15%的玻璃纤维。也称为：LNPThermoCompa化合物PF-1003产品再订购名称：PF003LNP ThermoCompa PF003化合物LNP ThermoCompa PF003是一种基于含玻璃纤维的尼龙6树脂的化合物。也称为：lnpThermocomp化合物pf-1003产品再订购名称：pf003 LNP™ THERMOCOMP™ PF003 compound LNP THERMOCOMP PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1003 Product reorder name: PF003 LNP™ THERMOCOMP™ PF003 compound LNP THERMOCOMP PF003 is a compound based on Nylon 6 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1003 Product reorder name: PF003	PA 6，15%玻璃纤维，注塑成型 Durethan® BKV15 000000 DUS008 (Dry) PA 6, 15 % glass fibers, injection molding Durethan® BKV15 000000 DUS008 PA 6, 15 % glass fibers, injection molding Durethan® BKV15 000000 DUS008 PA 6, 15 % glass fibers, injection molding

产品描述
厂家：	沙特沙伯基础 SABIC	德国恩骅力 Envalior
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 15	玻璃纤维 15
用途：
性能特点：
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

密度
Density g/cm³ ASTM D792

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：280℃，2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：280℃，2.0 mm)
Shrinkage rate %

机械性能
MECHANICAL LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂，23℃)
Tensile strain %

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量(23℃)
Tensile modulus MPa

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

热性能
THERMAL LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(3.00mm)
Flame retardant level UL-94

阻燃等级(6.00mm)
Flame retardant level UL-94

冲击性能
IMPACT LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

补充信息
LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

加工方式

注射 LNP™ THERMOCOMP™ PF003 compound Durethan® BKV15 000000 DUS008 单位测试方法

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3. 60x60x2mm, 4 hr

4. 60x60x2mm, 80°C MT, 600 bar

5. 2.0 mm/min

6. 2 mm/min

7. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
阻燃性能
冲击性能
补充信息
加工方式
注射
备注
返回顶部

PA6，LNP™ THERMOCOMP™ PF003 compound对比PA6，Durethan® BKV15 000000 DUS008对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别