牌号信息	RANPELEN SB-520Y 物性表 PP共聚 & 韩国乐天指导价格：暂无塑料库存：缺货	Polycomp® 6017 物性表 PP共聚 & 澳大利亚PolyPacific 指导价格：暂无塑料库存：缺货
牌号简介	RANPELEN SB-520Y是一种无规共聚聚丙烯吹塑成型，透明度好，光泽好，适用于医疗瓶。本产品可由输液瓶注射拉伸吹塑设备加工而成。RANPELEN SB-520Y具有很高的清晰度、合理的柔性刚度和较高的热变形温度，经蒸汽灭菌处理后能保持形状和透明度，并通过了美国药典六级检验。该等级在FDA DMF（药物主文件）注册，注册号为26629。 SB-520Y is random copolymer polypropylene for blow molding with good transparency and good gloss for medical bottle. This product can be processed by Injection stretch blow molding equipment for IV solution bottle. SB-520Y offers very high clarity, reasonable flexible stiffness and high heat distortion temperature result in maintaining shape and transparence after steam sterilization treatment and has passed the USP class VI tests. This grade is registered at FDA DMF (Drug Master Files) and registration number is 26629.	Polycomp® 6017是一种未填充的低流动聚丙烯共聚物化合物。它已开发用于需要长期暴露在高温和压力下的塑件。 Polycomp 6017 is an unfilled low flow polypropylene copolymer compound. It has been developed for mouldings requiring long term exposure to water at elevated temperatures and pressures.

产品描述
厂家：	韩国乐天 LOTTE	澳大利亚PolyPacific
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：
用途：	吹塑成型应用,医疗/护理用品	配件
性能特点：	机械强度好,透光性好,蒸汽消毒,无规共聚物 Good Rigidity,Good Clarity,Steam sterilized,Random copolymer	流动性低,共聚物 Low liquidity,Copolymer
加工条件：	注塑拉伸吹塑 Injection Stretch Blow Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL RANPELEN SB-520Y Polycomp® 6017 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL RANPELEN SB-520Y Polycomp® 6017 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(3 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，3 mm)
Tensile strain % ASTM D638

拉伸强度(3 mm)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

洛氏硬度(R 级，3.00 mm)
Rockwell hardness ASTM D785

邵氏硬度(邵氏 D，15 秒，3.00 mm)
Shore hardness

邵氏硬度(邵氏 D，3.00 mm)
Shore hardness

冲击性能
IMPACT RANPELEN SB-520Y Polycomp® 6017 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL RANPELEN SB-520Y Polycomp® 6017 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，3.0 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-30~30℃，3.00 mm)
Linear coefficient of thermal expansion 1/℃ ASTM D696

光学性能
OPTICAL RANPELEN SB-520Y Polycomp® 6017 单位
UNIT 测试方法
TEST METHOD

雾度
Haze % ASTM D1003

加工方式

注射 RANPELEN SB-520Y Polycomp® 6017 单位测试方法

加工熔体温度 °C

建议的最大回制料比例 %

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2. 50 mm/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
光学性能
加工方式
注射
备注
返回顶部