PS(HIPS)，STYRON A-TECH™ 1110对比PS(HIPS)，POLYREX® PH-888H物性表,价格行情_搜料

牌号信息	STYRON A-TECH™ 1110 物性表 PS(HIPS) & 美国盛禧奥指导价格：暂无塑料库存：缺货	POLYREX® PH-888H 物性表 PS(HIPS) & 台湾奇美指导价格：暂无塑料库存： 3000kg
牌号简介	"STYRON A-TECH™ 1110 抗冲改性聚苯乙烯是一种应用于注塑产品的高光泽度、高冲击强度的树脂。主要特性：优异的韧性光泽度高应用领域：小型家用电器玩具打印机遥控器符合以下法规：美国食品和药物管理局法规 21 CFR 177.1640 请查询法规以获取完备的细节资料。" STYRON A-TECH™ 1110 advanced technology polystyrene resin is a high-gloss, high-impact resin for injection molding applications. Main Characteristics: Excellent toughness High gloss Applications: Small appliances Toys Printers Remote controls Complies with: U.S. FDA 21 CFR 177.1640 Consult the regulation for complete details.	POLYREX® PH-888H是一种高抗冲聚苯乙烯产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。特性包括: 阻燃/额定火焰通过 ROHS 认证耐热 POLYREX® PH-888H is a High Impact Polystyrene product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Heat Resistant

产品描述
厂家：	美国盛禧奥 Trinseo	台湾奇美 CHI MEI
类别：	PS(HIPS) PS (HIPS)	PS(HIPS) PS (HIPS)
填料：
用途：	电器用具,玩具,商务设备
性能特点：	韧性好,表面光泽度好,冲击性能好,防火阻燃等级HB Good flexibility,Good surface appearance,High impact resistance,HB	耐高温,防火阻燃等级HB High Heat Resistance,HB
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183-3

密度(23℃)
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % ISO 294-4

收缩率(MD)
Shrinkage rate % ASTM D955

熔体体积流动速率(200℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(模压成型)
bending strength MPa ASTM D790

弯曲强度(注塑成型)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(模压成型)
Bending modulus MPa ASTM D790

弯曲模量(注塑成型)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ISO 527-2 3

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2 3

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸应变(断裂，注塑成型)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2 3

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(屈服，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂，注塑成型)
tensile strength MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-2 3

拉伸模量(模压成型)
Tensile modulus MPa ASTM D638

拉伸模量(注塑成型)
Tensile modulus MPa ASTM D638

洛氏硬度(L 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，模压成型)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度(-30℃)
Charpy impact strength kJ/m² ISO 179/1eU 3

简支梁冲击强度(23℃)
Charpy impact strength kJ/m² ISO 179/1eU 3

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

落锤冲击(23℃)
Drop hammer impact J ASTM D3029

热性能
THERMAL STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 3

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 3

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(--)
Linear coefficient of thermal expansion cm/cm/℃ ASTM D696

线性热膨胀系数(--)
Linear coefficient of thermal expansion cm/cm/℃ ISO 11359-2 3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度(A50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 3

阻燃性能
FLAMMABILITY STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.10 mm)
Flame retardant level ISO 1210 3

光学性能
OPTICAL STYRON A-TECH™ 1110 POLYREX® PH-888H 单位
UNIT 测试方法
TEST METHOD

光泽度(60°)
gloss ASTM D523

加工方式

注射 STYRON A-TECH™ 1110 POLYREX® PH-888H 单位测试方法

保压 MPa

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。

1 一般属性：这些不能被视为规格。

2 23°C

3 0.24 in/min

4 0.11 in/min

5 0.079 in/min

6 速率 A (50°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
光学性能
加工方式
注射
备注
返回顶部

PS(HIPS)，STYRON A-TECH™ 1110对比PS(HIPS)，POLYREX® PH-888H对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别