PC，ICORENE® 9909对比PC，SABIC® PC PC1800 resin物性表,价格行情_搜料

牌号信息	ICORENE® 9909 物性表 PC & 美国ICO Polymers 指导价格：暂无塑料库存：缺货	SABIC® PC PC1800 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	ICORENE® 9909是一种聚碳酸酯粉末，专门用于旋转成型。这一等级表现出良好的透明度、刚度和韧性的平衡。ICORENE® 9909是紫外线稳定的，适用于需要耐高温的应用。此外，ICORENE® 9909是UL94v2阻燃剂（Schulman研发测试）。 ICORENE® 9909 is a polycarbonate powder that has been specifically developed for rotational moulding. This grade exhibits an excellent balance of transparency, stiffness and toughness. ICORENE® 9909 is UV stabilised and is suitable for applications requiring high temperature resistance. Moreover, this grade is UL94 V2 flame retardant (Schulman R&D test).	SABIC PC PC1800树脂PC1800树脂是一种中高流量（300°C/1.2kg时，mfr=18）热稳定聚碳酸酯产品，设计用于定制复合市场。不含紫外线稳定剂或脱模剂。仅在www.sabicpc.com上提供。 PC1800 resin is a medium-high flow (MFR = 18 at 300°C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It is available exclusively at www.sabicpc.com.

产品描述
厂家：	美国ICO Polymers	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	照明装置	复合
性能特点：	机械强度好,耐候抗UV,透光性好,韧性好,阻燃,耐高温,防火阻燃等级V-2 Good Rigidity,Weather resistance is good,Good Clarity,Good flexibility,Flame Characteristics,High Heat Resistance,V-2	耐候抗UV,流动性中等,热稳定性好,防火阻燃等级V-2 Weather resistance is good,Moderate liquidity,Heat Stabilized,V-2
加工条件：	滚塑成型	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

热性能
THERMAL ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177, ISO 8302

导热系数(23℃)
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(-40 到 95℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(23 到 80℃)
Linear coefficient of thermal expansion cm/cm/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306/B50, ASTM D1525 15

阻燃性能
FLAMMABILITY ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level 内部方法

阻燃等级(1.50 mm)
Flame retardant level UL 94

光学性能
OPTICAL ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542，ISO 489

透光率(2540 µm)
Transmittance % ASTM D1003

透光率(3000 µm)
Transmittance % ISO 13468

雾度(2540 µm)
Haze % ASTM D1003

冲击性能
IMPACT ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ASTM D4812, ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

电气性能
ELECTRICAL ICORENE® 9909 SABIC® PC PC1800 resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant

介电常数(60 Hz)
Dielectric constant

介电强度(1.6 mm)
Dielectric strength kV/mm ASTM D149，IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257，IEC 60093

耗散因数(1 MHz)
Dissipation factor

耗散因数(60 Hz)
Dissipation factor

加工方式

注射 ICORENE® 9909 SABIC® PC PC1800 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2.0 in/min

4 类型 1, 2.0 in/min

5 0.051 in/min

6 0.079 in/min

7 Yield

8 80*10*3

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
阻燃性能
光学性能
冲击性能
电气性能
加工方式
注射
备注