牌号信息	PRE-ELEC® PP 1381 物性表 PP & 芬兰普宓斯指导价格：暂无塑料库存：缺货	SLOVALEN® PC 18 FRT 5 物性表 PP & 斯洛伐克Plastcom 指导价格：暂无塑料库存：缺货
牌号简介	PRE-ELEC® PP 1381是一种基于聚丙烯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。PRE-ELEC® PP 1381含有高含量的炭黑，可使用未经处理或回收的聚丙烯稀释至50%。实际用量应始终进行测试，因为它还取决于加工条件。PRE-ELEC® PP 1381适用于注塑产品。它是一种成本效益高的大型塑件解决方案，如箱子、板条箱和托盘。 PRE-ELEC® PP 1381 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. PRE-ELEC® PP 1381 contains a high load of carbon black and it can be diluted up to 50% with virgin or recycled PP. The actual amount should always be tested as it also depends on the processing conditions. PRE-ELEC® PP 1381 is intended for injection moulded products. It is cost-effective solution for big mouldings e.g. boxes, crates and pallets.	挤出用改性共聚物PP，含有机械性能改性剂和无卤无磷阻燃剂。以自然模式和完整RAL色标交付。 Modified copolymer PP for extrusion, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Delivered in natural mode and in the full RAL colour scale.

产品描述
厂家：	芬兰普宓斯 Premix Oy	斯洛伐克Plastcom
类别：	PP PP not specified	PP PP not specified
填料：
用途：	装货箱,托盘,容器
性能特点：	导电 Conductive	无卤,阻燃,化学耦合,共聚物,低磷含量,热稳定性好,防火阻燃等级V-0 Halogen free,Flame Characteristics,Chemical coupling,Copolymer,Low to no phosphorus content,Heat Stabilized,V-0
加工条件：	注射成型 Injection Molding	挤出 Extrusion

技术参数

物理性能
PHYSICAL PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(--)
Shrinkage rate % ISO 294-4

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

冲击性能
IMPACT PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-20℃，4mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，4mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ASTM D256 , ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648，ISO 75-2/B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B

维卡软化温度(A50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 2 , ISO 306/B50 2

电气性能
ELECTRICAL PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms ESD STM11.11，IEC 61340-2-3

机械性能
MECHANICAL PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(4 mm)
Bending modulus MPa ASTM D790

弯曲模量(4 mm)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(4 mm)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240 , ISO 868

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240 , ISO 868

阻燃性能
FLAMMABILITY PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

加工方式

注射 PRE-ELEC® PP 1381 SLOVALEN® PC 18 FRT 5 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 速率 A (50°C/h), 载荷2 (50N)

3 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
机械性能
阻燃性能
加工方式
注射
备注
返回顶部

PP，PRE-ELEC® PP 1381对比PP，SLOVALEN® PC 18 FRT 5对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别