PP共聚，SABIC® PP PCGR02对比PP共聚，DuClear® CE 85 B物性表,价格行情_搜料

牌号信息	SABIC® PP PCGR02 物性表 PP共聚 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	DuClear® CE 85 B 物性表 PP共聚 & 荷兰Ducor 指导价格：暂无塑料库存：缺货
牌号简介	SABIC用于医疗应用的PP等级在受控条件下生产，从而获得高质量、一致性和高纯度。SABIC® PP PCGR02是一种聚丙烯无规共聚物，主要为广泛的吹塑和挤出应用而开发，如单层和共挤出薄膜，用于医疗行业。该牌号具有良好的接触透明性、冲击强度和加工性能。典型应用：挤压/注射吹塑制成的瓶子和容器 SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGR02 is a polypropylene random copolymer primarily developed for a broad range of blow moulded and extrusion applications, such as monolayer and co-extruded films, for the healthcare industry. The grade exhibits a good contact transparency, good impact strength and an excellent processability. Typical applications: Bottles and containers made by extrusion / injection blow moulding	DuClear® CE 85 B是一种用于挤出应用的澄清聚丙烯无规共聚物（用邻苯二甲酸盐无催化剂生产）。该等级显示出高透明度和接触透明度，非常好的光泽和表面光洁度。DuClear® CE 85 B的主要应用是挤出吹塑、片材挤出和热成型。应用DuClear® CE 85 B适用于：消费品（如清洁剂、化妆品）吹塑瓶、工业用瓶。 DuClear CE 85 B is a clarified polypropylene random copolymer (produced with a phthalate-free catalyst) for extrusion applications. The grade exhibits high transparency and contact clarity, very good gloss and surface finish. The main applications of DuClear CE 85 B are extrusion blow molding, sheet extrusion and thermoforming. Applications DuClear CE 85 B is suitable for: blow molded bottles for consumer goods (e.g. detergents, cosmetics), bottles for industrial use

产品描述
厂家：	沙特沙伯基础 SABIC	荷兰Ducor
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：
用途：	瓶子,医疗/护理用品,容器	瓶子
性能特点：	易加工,透光性好,高纯度,冲击性能好,宽分子量分布,无规共聚物 Excellent Processability,Good Clarity,High purity,High impact resistance,Wide molecular weight distribution,Random copolymer	透光性好,表面光泽度好,无规共聚物 Good Clarity,Good surface appearance,Random copolymer
加工条件：	挤出 Extrusion	热成型 Thermo forming

技术参数

物理性能
PHYSICAL SABIC® PP PCGR02 DuClear® CE 85 B 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL SABIC® PP PCGR02 DuClear® CE 85 B 单位
UNIT 测试方法
TEST METHOD

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(--)
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(1% 正割)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT SABIC® PP PCGR02 DuClear® CE 85 B 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(0℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(0℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(0℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL SABIC® PP PCGR02 DuClear® CE 85 B 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

光学性能
OPTICAL SABIC® PP PCGR02 DuClear® CE 85 B 单位
UNIT 测试方法
TEST METHOD

雾度(1000 µm)
Haze % ASTM D1003

备注

1 一般属性：这些不能被视为规格。

2 0.039 in/min

3 2.0 in/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
光学性能
加工方式
备注