PPS，Fortron® 4332L6对比PPS，Fortron® 4184L4物性表,价格行情_搜料

牌号信息	Fortron® 4332L6 物性表 PPS & 美国塞拉尼斯指导价格：88200.0元/吨塑料库存： 5000kg	Fortron® 4184L4 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存：缺货
牌号简介	Fortron® 4332L6是一种玻璃纤维/矿物填充注塑等级，与其他gf/min增强PPS等级相比，该等级适用于需要改善拉伸和弯曲性能的应用。推荐的加工参数与标准等级相似。 Fortron 4332L6 is a glass fiber/mineral filled injection molding grade, which is intended for applications requiring improved tensile and flexural properties, when compared to other GF/MIN reinforced PPS grades. The recommended processing parameters are similar to the standard grades.	Fortron® 4184L4是目前最坚固和最坚硬的玻璃/矿物增强产品。它在高负荷下具有优异的耐热性和良好的耐化学性。电气性能优良，产品本身具有阻燃性。该产品还提供低蠕变阻力和良好的刚性，由于矿物含量。这种等级的应用包括电子元件（即线轴、连接器和电磁阀）。 Fortron 4184L4 is the strongest and toughest glass/mineral reinforced product available. It offers excellent heat resistance at high loads and good chemical resistance. The electrical properties are excellent and the product is inherently flame-retardant. This product also offers low creep resistance and good rigidity due to the mineral content. Applications made of this grade include electronic components (i.e. bobbins, connectors and solenoid valves).

产品描述
厂家：	美国塞拉尼斯 Celanese	美国塞拉尼斯 Celanese
类别：	PPS PPS	PPS PPS
填料：	玻璃纤维/矿物	玻璃纤维/矿物
用途：		电气/电子应用领域,连接器,阀门/阀门部件
性能特点：		机械强度好,韧性好,电气性好,阻燃,耐高温,耐化学性,防火阻燃等级V-0 Good Rigidity,Good flexibility,Good Electrical Properties,Flame Characteristics,High Heat Resistance,Solvent resistance,V-0
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

Specific Heat Capacity of Melt
Specific Heat Capacity of Melt J/kg/℃ Internal Method

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

特定体积
Specific volume cm³/g ASTM D792

机械性能
MECHANICAL Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

压缩强度(1% 应变，23℃)
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(60 Hz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

补充信息
Fortron® 4332L6 Fortron® 4184L4 单位
UNIT 测试方法
TEST METHOD

Specimen Thickness(Shrinkage)
Specimen Thickness（Shrinkage） mm Internal Method

加工方式

注射 Fortron® 4332L6 Fortron® 4184L4 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

螺杆长径比

备注

1 一般属性：这些不能被视为规格。

2 Break

3 10°C/min

4 方法B（逐步）


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注