POM共聚，LNP™ LUBRICOMP™ KFL25 compound对比POM共聚，LNP™ LUBRICOMP™ KFL36 compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ KFL25 compound 物性表 POM共聚 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ KFL36 compound 物性表 POM共聚 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP™ LUBRICOMP™ KFL25 compound 是一种基于缩醛共聚物树脂的化合物，含有25%的玻璃纤维和10%的聚四氟乙烯。这种材料的附加特征是：耐磨。又名：lnplubricomp化合物KFL-4025产品再订购名称：KFL25 LNP LUBRICOMP* KFL25 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4025 Product reorder name: KFL25	lnp lubricomp kfl36化合物lnp lubricomp kfl36是一种基于缩醛共聚物树脂的化合物，含有30%玻璃纤维、15%聚四氟乙烯。这种材料的附加特征是：耐磨。 LNP™ LUBRICOMP™ KFL36 compound LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4036 Product reorder name: KFL36 LNP™ LUBRICOMP™ KFL36 compound LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KFL-4036 Product reorder name: KFL36 LNP™ LUBRICOMP™ KFL36 compound LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound KFL-4036 Product reorder name: KFL36

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：	PTFE/玻璃纤维 10:25	PTFE/玻璃纤维 15:30
用途：
性能特点：	润滑性,耐磨 Lubricating,Good wear resistance	润滑性,耐磨 Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ KFL25 compound LNP™ LUBRICOMP™ KFL36 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ KFL25 compound LNP™ LUBRICOMP™ KFL36 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ KFL25 compound LNP™ LUBRICOMP™ KFL36 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ KFL25 compound LNP™ LUBRICOMP™ KFL36 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

加工方式

注射 LNP™ LUBRICOMP™ KFL25 compound LNP™ LUBRICOMP™ KFL36 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2.0 in/min

4 类型 1, 0.20 in/min

5 0.051 in/min

6 0.079 in/min

7 Break

8 80*10*4

9 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

POM共聚，LNP™ LUBRICOMP™ KFL25 compound对比POM共聚，LNP™ LUBRICOMP™ KFL36 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别