LMDPE，Clearflex® FH 50对比LMDPE，Clearflex® H&T FHH 508物性表,价格行情_搜料

牌号信息	Clearflex® FH 50 物性表 LMDPE & 意大利Versalis 指导价格：暂无塑料库存：缺货	Clearflex® H&T FHH 508 物性表 LMDPE & 意大利Versalis 指导价格：暂无塑料库存：缺货
牌号简介	Clearflex® FH 50是一种线性中等密度聚乙烯，含抗氧化剂，适用于吹塑薄膜挤出。用Clearflex® FH 50制造的薄膜具有良好的韧性和刚度平衡、耐高温和最佳密封性能。Clearflex® FH 50由于其高机械性能和良好的加工性能，被推荐用于共挤生产刚性好的薄膜。此外，它的凝胶含量非常低，使得树脂适合层压。 Clearflex FH 50 is a linear medium density polyethylene, with antioxidants, suitable for blown film extrusion. Films manufactured with Clearflex FH 50 are characterised by a good balance between toughness and rigidity, have high temperature resistance together with optimum sealing properties. Main Application Due to its high mechanical properties and excellent processability, Clearflex FH 50 is recommended in coextrusion for the production of film having good rigidity. Moreover, its very low gel content makes the resin ideal for lamination.	Clearflex H&T FHH 508是一种含抗氧化剂的辛烯共聚物线性中等密度聚乙烯，适用于吹塑薄膜挤出。由Clearflex H&T FHH 508制得的薄膜具有良好的光学性能、高刚性、耐高温和良好的密封性能。主要应用于其优异的光学性能和密封性能，以及极低的凝胶含量，CelfFLX H&T FHH 508是生产层压薄膜的理想选择。由于其软化点，Clearflex H&T FHH 508特别推荐用于必须承受热循环的软包装，如在薄膜中烹饪。 Clearflex H&T FHH 508 is an octene copolymer linear medium density polyethylene, with antioxidants, suitable for blown film extrusion. Films obtained from Clearflex H&T FHH 508 show good optical properties, high rigidity, high temperature resistance and excellent sealing properties. Main Application For its excellent optical properties and sealing performances, together with a very low gel content, Clearflex H&T FHH 508 is the ideal choice for the production of lamination films. Due to its softening point, Clearflex H&T FHH 508 is especially recommended for flexible packaging that have to withstand heat cycles such as cook-in films.

产品描述
厂家：	意大利Versalis	意大利Versalis
类别：	LMDPE LMDPE	LMDPE LMDPE
填料：
用途：	薄膜,层压板	包装,薄膜,层压板
性能特点：	易加工,韧性好,热封性好,低速凝固晶点,食品接触,耐高温,抗氧化 Excellent Processability,Good flexibility,Good heat sealing,Low speed solidification point,Food contact compliance,High Heat Resistance,Inoxidizability	机械强度好,韧性好,热封性好,光学性能,低速凝固晶点,食品接触,耐高温,抗氧化,辛烯共聚单体,共聚物 Good Rigidity,Good flexibility,Good heat sealing,Optical performance,Low speed solidification point,Food contact compliance,High Heat Resistance,Inoxidizability,Octene copolymer,Copolymer
加工条件：	吹塑薄膜	吹塑薄膜

技术参数

物理性能
PHYSICAL Clearflex® FH 50 Clearflex® H&T FHH 508 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Clearflex® FH 50 Clearflex® H&T FHH 508 单位
UNIT 测试方法
TEST METHOD

摩擦系数(与自身 - 动态，吹塑薄膜)
friction coefficient ISO 8295

薄膜
Clearflex® FH 50 Clearflex® H&T FHH 508 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂，25 µm，吹塑薄膜)
Tensile strain %

拉伸应变(TD，断裂，25 µm，吹塑薄膜)
Tensile strain %

拉伸强度(MD，屈服，25 µm，吹塑薄膜)
tensile strength MPa

拉伸强度(MD，断裂，25 µm，吹塑薄膜)
tensile strength MPa

拉伸强度(TD，屈服，25 µm，吹塑薄膜)
tensile strength MPa

拉伸强度(TD，断裂，25 µm，吹塑薄膜)
tensile strength MPa

拉伸模量(1% 正割，MD，25 µm，吹塑薄膜)
Tensile modulus MPa

拉伸模量(1% 正割，TD，25 µm，吹塑薄膜)
Tensile modulus MPa

撕裂强度(MD，25 µm)
tear strength kN/m

撕裂强度(TD，25 µm)
tear strength kN/m

落锤冲击(25 µm，吹塑薄膜)
Drop hammer impact g ISO 7765-1

薄膜厚度
film thickness

薄膜厚度(测试)
film thickness µm

热性能
THERMAL Clearflex® FH 50 Clearflex® H&T FHH 508 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ 内部方法

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

脆化温度
Embrittlement temperature ℃ ASTM D746

光学性能
OPTICAL Clearflex® FH 50 Clearflex® H&T FHH 508 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，25 µm，吹塑薄膜)
gloss ASTM D2457

雾度(25 µm，吹塑薄膜)
Haze % ISO 14782

加工方式

挤出 Clearflex® FH 50 Clearflex® H&T FHH 508 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 F50

3 Blown Film

1 一般属性：这些不能被视为规格。

2 F50

3 Blown Film


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
薄膜
热性能
光学性能
加工方式
挤出
备注
返回顶部