PA12，EOS PA 3200 GF对比PA12，Rilsamid® AZM 23 Noir T6LD物性表,价格行情_搜料

牌号信息	EOS PA 3200 GF 物性表 PA12 & 德国EOS 指导价格：暂无塑料库存：缺货	Rilsamid® AZM 23 Noir T6LD 物性表 PA12 & 法国阿科玛指导价格：暂无塑料库存：缺货
牌号简介	PA 3200 GF是一种白色的玻璃填充聚酰胺12粉末，其特点是具有良好的刚度和良好的断裂延伸率。由PA 3200 GF制成的激光烧结零件具有优良的材料性能：高硬度、高机械耐磨性、良好的热负荷性、优异的表面质量、高尺寸精度和细节分辨率、良好的可加工性、优异的长期恒定性能。PA 3200 GF的典型应用是用于Fina。l汽车发动机区域内的零件，用于深冲模具或任何其他需要特殊刚度、高热变形温度和低磨损的应用。 PA 3200 GF is a whitish, glass-filled polyamide 12 powder, which is characterised by an excellent stiffness in combination with good elongation at break. Laser-sintered parts made from PA 3200 GF possess excellent material properties: high stiffness high mechanical wear-resistance good thermal loadability excellent surface quality high dimensional accuracy and detail resolution good processability excellent long-term constant behaviour A typical application for PA 3200 GF is the usage e.g. for final parts within the engine area of cars, for deep-drawing dies or any other application which requires particular stiffness, high heat distortion temperature and low abrasive wear.	Rilsamid AZM 23 Noir T6LD是一种玻璃纤维增强聚酰胺12。这个黑色等级是为注射而设计的。主要应用快速连接器。 Rilsamid® AZM 23 BLACK T6LD resin is a fiberglass reinforced polyamide. This black colored grade is designed for injection moulding.

产品描述
厂家：	德国EOS	法国阿科玛 Arkema
类别：	PA12 PA12	PA12 PA12
填料：	玻璃纤维	玻璃纤维
用途：	汽车的发动机罩下的零件,汽车领域的应用,工程配件	连接器
性能特点：	机械强度好,易加工,表面光泽度好,低摩擦系数,耐高温,拉伸性能好,耐磨 Good Rigidity,Excellent Processability,Good surface appearance,Low coefficient of friction,High Heat Resistance,Good Tensile Strength,Good wear resistance
加工条件：	3D Printing, Laser Sintering/Melting 3D Printing, Laser Sintering/Melting	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ 内部方法

熔体体积流动速率(235℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

冲击性能
IMPACT EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357

熔融温度
Melting temperature ℃ ISO 11357-3

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(--)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa ISO 527-2

球压硬度
Ball hardness MPa ISO 2039-1

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，15 秒)
Shore hardness ISO 868

补充信息
EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 1874

加工方式

注射 EOS PA 3200 GF Rilsamid® AZM 23 Noir T6LD 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Z Direction

3 X Direction

4 Y Direction

5 20°C/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
补充信息
加工方式
注射
备注
返回顶部

PA12，EOS PA 3200 GF对比PA12，Rilsamid® AZM 23 Noir T6LD对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别