PC，Canuck Compounds 700 Series - BK 7-9-5对比PC，LEXAN™ EXL8134 resin物性表,价格行情_搜料

牌号信息	Canuck Compounds 700 Series - BK 7-9-5 物性表 PC & 加拿大Canuck Compounders 指导价格：暂无塑料库存：缺货	LEXAN™ EXL8134 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Canuck Compounds 700 Series - BK 7-9-5是一种聚碳酸酯（PC）材料,。加工方式为:注射成型。 Canuck Compounds 700 Series - BK 7-9-5 is a Polycarbonate (PC) material. It is available in North America for injection molding.	LEXAN EXL8134是一种高流动性、优异的低温冲击性和30%消费后回收率的PC/硅氧烷共聚物树脂。仅限有限的可用性和有限的颜色。在批准应用前，需要考虑更高的颜色变异性和污染风险，包括黑色规格。 LEXAN EXL8134 is a PC/siloxane copolymer resin with high flow, excellent low temperature impact and 30% post consumer recycle content. Limited availability and restricted color only. Higher color variability and contamination risks including black specs needs to be considered before approval for use in applications.

产品描述
厂家：	加拿大Canuck Compounders	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：
性能特点：		流动性高,共聚物,耐低温冲击,防火阻燃等级HB High liquidity,Copolymer,low-temperature impact resistance,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % 内部方法

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790A

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790-A

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain %

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain %

拉伸强度(屈服)
tensile strength MPa

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa

拉伸模量
Tensile modulus MPa ASTM D638

冲击性能
IMPACT Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

落锤冲击(23℃)
Drop hammer impact J ASTM D5420

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.35 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.35 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 6

电气性能
ELECTRICAL Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度(0.8 mm，在油中)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 MHz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃

阻燃等级(0.75 mm)
Flame retardant level UL 94

加工方式

注射 Canuck Compounds 700 Series - BK 7-9-5 LEXAN™ EXL8134 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 几何 GD

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 2,0 in/min

4 0,051 in/min

5 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注