牌号信息	China PPS PTFE-hGR312 物性表 PPS & 四川得阳指导价格：暂无塑料库存：缺货	China PPS PTFE-hGR203 物性表 PPS & 四川得阳指导价格：暂无塑料库存：缺货
牌号简介	PPS/PTFE-HGR312是一种润滑剂PPS化合物，由玻璃纤维、聚四氟乙烯和以PPS树脂为基础的成分填充而成。具有耐磨、耐溶剂、机械性能好、模量高、抗蠕变、耐高温、固有阻燃、易加工、模具收缩率低等特点。由于其高性能，在高温、高压、腐蚀性溶剂条件下制造磨损件，在化工、医药等行业得到广泛应用。也可用于机械行业塑料轴套、轴承、滑块的制造。 PPS/PTFE-hGR312 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows abrasive resistance, solvent resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage. Owing to its high performance, it's widely used in chemical and medical industry for making wearing pieces in corrosive solvent condition of high temperature, high pressure and corrosive solvent. It also can be used to make plastic axle sleeve, axle bearing and slide block in mechanical industry.	PPS/PTFE-HGR203是一种以PPS树脂为基础，填充玻璃纤维、聚四氟乙烯和各种成分的PPS润滑剂。具有耐溶剂、耐磨、机械性能好、模量高、抗蠕变、耐高温、固有阻燃、易加工、模具收缩率低、尺寸稳定性好等特点。由于其高性能，广泛应用于机械和化学工业中，用于制造高温、高压和溶剂环境下工作的易损件/部件。如：塑料轴承、轴套、纺织机械零部件、航空工业用零部件等。 PPS/PTFE-hGR203 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows solvent resistance, abrasive resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage, good dimensional stability. Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. Such as: plastic axle bearing, axle sleeve, textile machine components, components which are used in aero industry.

产品描述
厂家：	四川得阳 Deyang	四川得阳 Deyang
类别：	PPS PPS	PPS PPS
填料：	PTFE/玻璃纤维	PTFE/玻璃纤维
用途：	医疗/护理用品,工业应用	航空航天应用,医疗/护理用品,工业应用
性能特点：	易加工,韧性好,收缩性低,阻燃,耐高温,润滑性,耐磨,耐化学性,防火阻燃等级V-0 Excellent Processability,Good flexibility,Low contractility,Flame Characteristics,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance,V-0	易加工,尺寸稳定性好,收缩性低,阻燃,耐高温,润滑性,耐磨,耐化学性,防火阻燃等级V-0 Excellent Processability,Good Dimensional Stability,Low contractility,Flame Characteristics,High Heat Resistance,Lubricating,Good wear resistance,Solvent resistance,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ 内部方法

收缩率(MD)
Shrinkage rate % 内部方法

冲击性能
IMPACT China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² 内部方法

热性能
THERMAL China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ 内部方法

熔融温度
Melting temperature ℃ 内部方法

阻燃性能
FLAMMABILITY China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level 内部方法

机械性能
MECHANICAL China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位
UNIT 测试方法
TEST METHOD

Abrasion(Width)
Abrasion（Width） mm 内部方法

弯曲强度
bending strength MPa 内部方法

弯曲模量
Bending modulus MPa 内部方法

拉伸应变(断裂)
Tensile strain % 内部方法

拉伸强度
tensile strength MPa 内部方法

摩擦系数
friction coefficient 内部方法

洛氏硬度
Rockwell hardness 内部方法

磨损量
Wear amount mg 内部方法

加工方式

注射 China PPS PTFE-hGR312 China PPS PTFE-hGR203 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 120 min

3 HR

1 一般属性：这些不能被视为规格。

2 120 min

3 HR


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
加工方式
注射
备注
返回顶部