PA6，Nypol® PA B3 HL HV400 NTLA010 NT389对比PA6，Ultramid® 8270 HS物性表,价格行情_搜料

牌号信息	Nypol® PA B3 HL HV400 NTLA010 NT389 物性表 PA6 & 巴西Petropol 指导价格：暂无塑料库存：缺货	Ultramid® 8270 HS 物性表 PA6 & 德国巴斯夫指导价格：暂无塑料库存：缺货
牌号简介	聚酰胺6天然油，高粘度，用于薄膜挤出、管材和半成品。 Polyamide 6 natural oiled with high viscosity to filme extrusion, tubes and semi-finished products.	Ultramid® 8270 HS是一种热改性PA6吹塑复合材料，具有优异的韧性和熔融强度，非常适合吹塑、型材挤压和其他需要极高熔融粘度的应用。它对油、碳氢化合物和大多数溶剂具有良好的渗透性和耐化学性。应用Ultramid® 8270 HS通常推荐用于工业容器、小型汽油罐和汽车引擎盖下油箱等应用。 Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents. Applications Ultramid 8270 HS is generally recommended for applications such as industrial containers, small gasoline tanks, and automotive under hood reservoirs.

产品描述
厂家：	巴西Petropol	德国巴斯夫 BASF
类别：	PA6 PA6	PA6 PA6
填料：
用途：	薄膜,管件	油箱,汽车的发动机罩下的零件,工业容器
性能特点：	高粘度,防火阻燃等级HB High Viscosity,HB	高粘,熔体强度好,超高韧性,耐油,耐化学性,热稳定性好,耐碳氢化合物,防火阻燃等级HB,防火阻燃等级V-2 Ultra High Viscosity,Good melt strength,Ultra high toughness,Grease resistance,Solvent resistance,Heat Stabilized,Hydrocarbons,HB,V-2
加工条件：	薄膜挤出 Film extrusion	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(平衡)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

弯曲强度(-40℃)
bending strength MPa ASTM D790

弯曲强度(121℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(65℃)
bending strength MPa ASTM D790

弯曲强度(90℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(-40℃)
Bending modulus MPa ASTM D790

弯曲模量(121℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(65℃)
Bending modulus MPa ASTM D790

弯曲模量(90℃)
Bending modulus MPa ASTM D790

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服，-40℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，121℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃ ASTM D2117

熔融温度(DSC)
Melting temperature ℃ ISO 3146

相对温度指数(0.75 mm)
Relative temperature index ℃ UL 746

相对温度指数(6.0 mm)
Relative temperature index ℃ UL 746

相对温度指数(冲击机械性能)
Relative temperature index UL 746

相对温度指数(强度机械性能)
Relative temperature index UL 746

相对温度指数(电气性能)
Relative temperature index UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM E831

阻燃性能
FLAMMABILITY Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(6.00 mm)
Flame retardant level UL 94

补充信息
Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位
UNIT 测试方法
TEST METHOD

Blow Molding Drying Temperature
Blow Molding Drying Temperature ℃

Blow Molding Melt Temperature
Blow Molding Melt Temperature ℃

Blow Molding Moisture Content
Blow Molding Moisture Content %

Blow Molding Mold Temperature
Blow Molding Mold Temperature ℃

Blow Molding 干燥时间
Blow Molding drying time hr

Blow(up Ratio)
Blow（up Ratio）

加工方式

注射 Nypol® PA B3 HL HV400 NTLA010 NT389 Ultramid® 8270 HS 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

PA6，Nypol® PA B3 HL HV400 NTLA010 NT389对比PA6，Ultramid® 8270 HS对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别