ABS，POLYLAC® PA-747对比ABS，POLYLAC® PA-717C物性表,价格行情_搜料

牌号信息	POLYLAC® PA-747 物性表 ABS & 台湾奇美指导价格：18375.0元/吨塑料库存： 31025kg	POLYLAC® PA-717C 物性表 ABS & 台湾奇美指导价格：16778.0元/吨塑料库存： 5000kg
牌号简介	POLYLAC® PA-747是一种丙烯腈丁二烯苯乙烯(ABS)产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。特性包括: 阻燃/额定火焰通过 ROHS 认证耐冲击 POLYLAC® PA-747 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include: Flame Rated RoHS Compliant Impact Resistant	POLYLAC® PA-717C是一种丙烯腈丁二烯苯乙烯(ABS)产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。特性包括: 阻燃/额定火焰通过 ROHS 认证耐冲击 POLYLAC® PA-717C is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include: Flame Rated RoHS Compliant Impact Resistant

产品描述
厂家：	台湾奇美 CHI MEI	台湾奇美 CHI MEI
类别：	ABS	ABS ABS
填料：
用途：
性能特点：	冲击性能好,防火阻燃等级HB High impact resistance,HB	防火阻燃等级HB HB
加工条件：

技术参数

物理性能
PHYSICAL POLYLAC® PA-747 POLYLAC® PA-717C 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(23℃)
Density g/cm³ ISO 1183

成型收缩率
Molding Shrinkage % ISO 294-4

收缩率
Shrinkage rate % ISO 294-4

熔体体积流动速率(220℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL POLYLAC® PA-747 POLYLAC® PA-717C 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲模量
Flexural Modulus GPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸伸长率
Tensile Elongation % ISO 527

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
Tensile Strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
Tensile Strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT POLYLAC® PA-747 POLYLAC® PA-717C 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength KJ/m² ISO 180/1A

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength KJ/m² ISO 180/1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(-30℃)
Charpy notched Impact strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy notched Impact strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL POLYLAC® PA-747 POLYLAC® PA-717C 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-1/-2

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
HDT ℃ ISO 75-1/-2

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数
Coeff.of linear therm expansion ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 7

维卡软化温度(1 Kg,50 ℃/hr)
Vicat Softening Temperature ℃ ISO 306/B

维卡软化温度(5 Kg,50 ℃/hr)
Vicat Softening Temperature ℃ ISO 306/B

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY POLYLAC® PA-747 POLYLAC® PA-717C 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.5 mm)
Flame Class Rating UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 POLYLAC® PA-747 POLYLAC® PA-717C 单位测试方法

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

3 23°C

4 6.0 mm/min

5 2.8 mm/min

6 2.0 mm/min

7 速率 A (50°C/h), 压力1 (10N)

3 23°C

4 6.0 mm/min

5 2.8 mm/min

6 2.0 mm/min

7 速率 A (50°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注