PP均聚，POLIMAXX 2500H对比PP均聚，TOTAL Polypropylene PPC 3650物性表,价格行情_搜料

牌号信息	POLIMAXX 2500H 物性表 PP均聚 & 泰国IRPC 指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPC 3650 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	2500H是挤出成型和吹塑成型用聚丙烯嵌段共聚物树脂，尺寸稳定性好。它适用于任何需要高冲击强度的部件，如瓦楞纸板、固定片应用等。它也符合联邦食品药品管理局在21CFR 177.1520中关于食品接触的法规的要求。 2500H is a Polypropylene Block Copolymer resin for extrusion process and blow molding process with good dimensional stability. It is suitable for any parts that need high impact strength such as corrugated board, stationary sheets application, and etc. It also meets the F.D.A. requirement in the code of federal regulations in 21 CFR 177.1520 for food contact.	聚丙烯PPC 3650是一种异相共聚物，熔融流动指数为2 g/10 min。聚丙烯PPC 3650在韧性和流动性之间提供了极好的平衡，特别适用于大桶、面包和蔬菜托盘、板条箱和大桶等重型应用的注塑成型。 Polypropylene PPC 3650 is heterophasic copolymer with a Melt Flow Index of 2 g/10 min. Polypropylene PPC 3650 provides an excellent balance between toughness and flow, being particularly suitable in injection molding for heavy duty applications such as tote bins, bread & vegetable trays, crates and large pails.

产品描述
厂家：	泰国IRPC	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	文具,波形板,片材	装货箱,桶
性能特点：	冲击性能好,尺寸稳定性好,食品接触,嵌段共聚物 High impact resistance,Good Dimensional Stability,Food contact compliance,Block Copolymer	抗冲共聚物 Impact copolymer
加工条件：	吹塑成型	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POLIMAXX 2500H TOTAL Polypropylene PPC 3650 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT POLIMAXX 2500H TOTAL Polypropylene PPC 3650 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² DIN 53453

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL POLIMAXX 2500H TOTAL Polypropylene PPC 3650 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL POLIMAXX 2500H TOTAL Polypropylene PPC 3650 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(1% 正割)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

加工方式

挤出 POLIMAXX 2500H TOTAL Polypropylene PPC 3650 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
挤出
备注
返回顶部

PP均聚，POLIMAXX 2500H对比PP均聚，TOTAL Polypropylene PPC 3650对比物性表,价格行情_搜料_soliao