PBT，VALOX™ HX215HP resin对比PBT，LNP™ COLORCOMP™ HX215HPC compound物性表,价格行情_搜料

牌号信息	VALOX™ HX215HP resin 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ COLORCOMP™ HX215HPC compound 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	高流量，无加强，聚对苯二甲酸丁二醇酯（PBT）与模具释放。用于医疗设备和医药应用。卫生保健变更管理，生物相容性（ISO 10993或USP六级），符合食品接触。颜色有限。 High Flow, Unreinforced, Polybutylene Terephthalate (PBT) with mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors.	colorcomphx215hpc是一种基于PBT的化合物。附加功能包括：模具释放，用于医疗器械和制药应用。卫生保健变更管理，生物相容性（ISO 10993或USP六级），符合食品接触。 COLORCOMP HX215HPCis a compound based on PBT. Added features include: Mold Release, for use in medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：
用途：	药物,医疗/护理用品	医疗器械,药物
性能特点：	流动性高,生物兼容性,食品接触 High liquidity,Biocompatible,Food contact compliance	生物兼容性,含脱模剂,食品接触 Biocompatible,Good stripping performance,Food contact compliance
加工条件：	化合物挤出	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

加工方式

注射 VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

挤出 VALOX™ HX215HP resin LNP™ COLORCOMP™ HX215HPC compound 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)