PA6，Promyde® B30 P2 M30对比PA6，DOMAMID® 6LVT30H2 BK物性表,价格行情_搜料

牌号信息	Promyde® B30 P2 M30 物性表 PA6 & 西班牙NUREL 指导价格：暂无塑料库存：缺货	DOMAMID® 6LVT30H2 BK 物性表 PA6 & 德国道默指导价格：暂无塑料库存：缺货
牌号简介	Promyde® B30 P2 M30是一种聚酰胺6注塑级，30%矿物填料，热稳定。特点Promyde® B30 P2 M30具有高机械强度、硬度、刚性和热稳定性。由Promyde® B30 P2 M30制成的零件具有特别高的尺寸稳定性。应用Promyde® B30 P2 M30广泛应用于需要机械性能和尺寸稳定性组合的各种应用中。矿物填料增强等级适用于外壳、支架、工业物品和电气绝缘部件。 Promyde® B30 P2 M30 is a Polyamide 6 injection moulding grade with 30% mineral filler and heat stabilized. CHARACTERISTICS Promyde B30 P2 M30 is distinguished by high mechanical strength, hardness, rigidity and thermo stability. Parts made from Promyde B30 P2 M30 have particularly high dimensional stability. APPLICATIONS Promyde B30 P2 M30 is used in a wide range of applications where a combination of mechanical properties and dimensional stability is needed. Mineral filler reinforced grades are suitable for housings, supports, industrial articles and electrical insulating parts.	（Domamid A1-130-T30-H2-DB）聚酰胺6，低粘度，注塑等级，30%矿物增强，热稳定，黑色 (DOMAMID A1-130-T30-H2-DB) Polyamide 6, low viscosity, injection moulding grade, 30% mineral reinforced, heat stabilized, black

产品描述
厂家：	西班牙NUREL	德国道默 DOMO
类别：	PA6 PA6	PA6 PA6
填料：	矿物 30	矿物 30
用途：	外壳,工业应用,电子绝缘,电气/电子应用领域
性能特点：	尺寸稳定性好,防火阻燃等级HB,硬度高,机械强度好,热稳定性好 Good Dimensional Stability,HB,Good Hardness,Good Rigidity,Heat Stabilized	低粘度,热稳定性好 Low Viscosity,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³

密度
Density g/cm³ ISO 1183

收缩率(MD：23℃，72 hrs)
Shrinkage rate %

收缩率(TD：23℃，72 hrs)
Shrinkage rate %

熔体体积流动速率(275℃，5 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(275℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

粘数
Viscosity number cm³/g ISO 307

机械性能
MECHANICAL Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain %

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa

拉伸模量
Tensile modulus MPa

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 Promyde® B30 P2 M30 DOMAMID® 6LVT30H2 BK 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0,079 in/min

3 10°C/min

2. 50% RH

3. 5.0 mm/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部