牌号信息	RTP 178X 物性表 PP & 美国RTP 指导价格：暂无塑料库存：缺货	RTP 178 UV 物性表 PP & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。RTP 170系列材料的开发结合了良好的物理性能和可塑性，其中直玻璃填充，滑石填充或矿物填充材料将不起作用。RTP 178X与RTP 178相似，强度和成本略有降低。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 170 Series materials were developed to combine good physical properties and moldability where straight glass filled, talc filled or mineral filled materials will not do the job. RTP 178X is similar to RTP 178 with slightly reduced strengths and cost.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.

产品描述
厂家：	美国RTP	美国RTP
类别：	PP PP not specified	PP PP not specified
填料：
用途：
性能特点：	机械强度好,易加工,化学耦合,热稳定性好,防火阻燃等级HB Good Rigidity,Excellent Processability,Chemical coupling,Heat Stabilized,HB	化学耦合,防火阻燃等级HB Chemical coupling,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm，注塑成型)
Shrinkage rate % ASTM D955

收缩率(MD：6.35 mm，注塑成型)
Shrinkage rate % ASTM D955

冲击性能
IMPACT RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，注塑成型)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，注塑)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耐电弧性
Arc resistance sec ASTM D495

耐电弧性(1.59 mm)
Arc resistance sec ASTM D495

耗散因数(1 MHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

机械性能
MECHANICAL RTP 178X RTP 178 UV 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲强度(注塑成型)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(注塑成型)
Bending modulus MPa ASTM D790

拉伸应变(屈服，注塑成型)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(注塑成型)
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 RTP 178X RTP 178 UV 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 方法A（短时间）


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
备注
返回顶部