牌号信息	COSMOTHENE® F108-5 物性表 LDPE & 新加坡聚烯烃指导价格：暂无塑料库存：缺货	Lutene® FB0300 物性表 LDPE & 韩国LG化学指导价格：暂无塑料库存：缺货
牌号简介	COSMOTHENE® F108-5是专门设计的，具有优良的收缩、韧性和强度。F108-5不含防滑防堵剂。收缩膜食品包装、重型袋等。 COSMOTHENE F108-5 is specially design for excellent shrinkage, toughness and strength. F108-5 is not formulated with slip and antiblocking agent. Shrink film food packaging, heavy duty bag & etc.	鲁特尼FB0300主要用于挤出机械性能高的吹塑薄膜，用于制造重型包装袋和托盘收缩膜。叶黄素FB0300具有优良的机械性能和高的抗应力开裂性能，适用于重型袋和特殊的底封袋。（叶黄素FB0300不含滑动剂。）应用：重型产品包装、收缩罩、托盘收缩盖、所有类型的工业包装 LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the excellent mechanical properties and high stress cracking resistance make suitable for heavy duty bags and particularity bottom sealed bags. (LUTENE FB0300 contains no slip agent.) Applications: Packing of heavy products, Shrink hoods, Pallet shrink covers, all types of industrial packing

产品描述
厂家：	新加坡聚烯烃 TPC	韩国LG化学 LG Chemical
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	薄膜,收缩性薄膜,重包装袋	工业应用,包装,薄膜,收缩性薄膜,袋子
性能特点：	韧性好,收缩性高 Good flexibility,High shrinkage	抗应力开裂 High ESCR
加工条件：	挤出 Extrusion	吹塑薄膜

技术参数

物理性能
PHYSICAL COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度 Density
g/cm³ ASTM D792

抗环境应力开裂(F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体质量流动速率 Melt Flow Rate
g/10min ASTM D1238

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

弯曲模量 Flexural Modulus(23℃)
MPa ASTM D747

拉伸应变 Tensile Strain(断裂 brk)
% ASTM D638

拉伸强度 Tensile Strength(断裂 brk)
MPa ASTM D638

撕裂阻力(MD)
Tear resistance MPa ASTM D1922

撕裂阻力(TD)
Tear resistance MPa ASTM D1922

薄膜
COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂)
Tensile strain % ASTM D882

拉伸应变(TD，断裂)
Tensile strain % ASTM D882

拉伸强度(MD，断裂)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂)
tensile strength MPa ASTM D882

氮传输速率
Nitrogen transfer rate cm³/m²/24 hr 内部方法

水蒸气透过性
Water vapor permeability g/m²/24 hr 内部方法

落锤冲击
Drop hammer impact g ASTM D1709

薄膜厚度 film thickness(测试)
µm

薄膜厚度(测试)
film thickness µm

透氧率
Oxygen permeability cm³/m²/24 hr 内部方法

热性能
THERMAL COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ DSC

熔融温度 Melting temperature
℃ 内部方法

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

光学性能
OPTICAL COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

光泽度 Gloss(30 µm)
ASTM D2457

光泽度(60°)
gloss ASTM D2457

雾度
Haze % ASTM D1003

雾度 Haze(30 µm)
% ASTM D1003

补充信息
COSMOTHENE® F108-5 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

Slip(30.0 µm)
Tan θ 内部方法

阻塞力 Blocking force(30.0 µm)
g/100 cm² ASTM D3354

加工方式

挤出成型 Extrusion Molded COSMOTHENE® F108-5 Lutene® FB0300 单位测试方法

料筒-1区温度 Barrel - Zone 1 Temperature °C

料筒-2区温度 Barrel - Zone 2 Temperature °C

料筒-3区温度 Barrel - Zone 3 Temperature °C

模头温度 Die Temperature °C

熔体温度 Melt Temperature °C

挤出 COSMOTHENE® F108-5 Lutene® FB0300 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
薄膜
热性能
光学性能
补充信息
加工方式
挤出成型 Extrusion Molded
挤出
备注