PA66，LNP™ VERTON™ RV00AE compound对比PA66，Staramide RF00ASXP物性表,价格行情_搜料

牌号信息	LNP™ VERTON™ RV00AE compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Staramide RF00ASXP 物性表 PA66 & 美国奥升德指导价格：暂无塑料库存：缺货
牌号简介	LNP™ VERTON™ RV00AE化合物LNP™ VERTON™ RV00AE是一种基于尼龙66的化合物，含有50%长的玻璃纤维。这一级别的附加功能包括：容易成型，高刚度，低蠕变，美观的表面光洁度。 LNP™ VERTON™ RV00AE compound LNP VERTON RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound RF-700-10-EM Product reorder name: RV00AE LNP™ VERTON™ RV00AE compound LNP VERTON RV00AE is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding. Also known as: LNP* VERTON* Compound RF-700-10 EM Product reorder name: RV00AE	Staramide RF00ASXP是一种50%玻璃纤维增强聚酰胺66注塑树脂，热稳定（也称为淀粉酰胺66 G 50V S3） Staramide RF00ASXP is a 50 % Glass Fiber Reinforced Polyamide 66 Injection Molding Resin heat stabilized (also known as Staramide 66 G 50V S3)

产品描述
厂家：	沙特沙伯基础 SABIC	美国奥升德 Ascend
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 50	玻璃纤维 50
用途：	构件
性能特点：	易加工 Excellent Processability	热稳定性好,防火阻燃等级HB Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(MD：4.0 mm)
Shrinkage rate % 内部方法

收缩率(TD)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

热性能
THERMAL LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

阻燃性能
FLAMMABILITY LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75mm)
Flame retardant level UL-94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(3.00mm)
Flame retardant level UL-94

冲击性能
IMPACT LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

电气性能
ELECTRICAL LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位
UNIT 测试方法
TEST METHOD

热丝引燃(HWI)
Hot wire ignition UL 746

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

加工方式

注射 LNP™ VERTON™ RV00AE compound Staramide RF00ASXP 单位测试方法

加工熔体温度 °C

干燥时间 Hr

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度模头温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Break

7 80*10*4

8 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 Yield

4 80*10*4


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
阻燃性能
冲击性能
电气性能
加工方式
注射
备注
返回顶部

PA66，LNP™ VERTON™ RV00AE compound对比PA66，Staramide RF00ASXP对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别