PA66，Ultramid® A3EG7 BK23189对比PA66，Radiflam® A RV350 AF 333 NER物性表,价格行情_搜料

牌号信息	Ultramid® A3EG7 BK23189 物性表 PA66 & 德国巴斯夫指导价格：暂无塑料库存：缺货	Radiflam® A RV350 AF 333 NER 物性表 PA66 & 意大利兰蒂奇指导价格：暂无塑料库存：缺货
牌号简介	Ultramid® A3EG7 BK23189是一种35%玻璃纤维增强，色素黑色，注塑成型PA66级机械部件和外壳的高硬度和尺寸稳定性。典型应用包括灯插座外壳、冷却风扇、铝窗框的绝缘轮廓、汽车冷却系统的水容器以及电绝缘部件。 Ultramid A3EG7 BK23189 is a 35% glass fiber reinforced, pigmented black, injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts.	PA66阻燃注射成型级红磷。35%玻璃纤维增强。黑色。适用于要求阻燃、刚度高、机械阻力好的零件。根据UL-94，0.75 mm下的额定V-0。ISO 1043:PA66 GF35 FR（52+72） PA66 flame retardant injection moulding grade with red phosphorus. 35% glass fiber reinforced. Black colour. Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Rated V-0 at 0.75 mm according to UL-94. ISO 1043 : PA66 GF35 FR(52+72)

产品描述
厂家：	德国巴斯夫 BASF	意大利兰蒂奇 Radici
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 35	玻璃纤维 35
用途：	汽车领域的应用,电子绝缘,容器,外壳,机器/机械部件
性能特点：	机械强度好,尺寸稳定性好,耐油 Good Rigidity,Good Dimensional Stability,Grease resistance	机械强度好,阻燃,防火阻燃等级V-0 Good Rigidity,Flame Characteristics,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH，2.00 mm)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

吸水率(饱和，23℃，2.00 mm)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

机械性能
MECHANICAL Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位
UNIT 测试方法
TEST METHOD

0.80 mm
0.80 mm UL 94

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

燃烧速率
Burning rate mm/min FMVSS 302

加工方式

注射 Ultramid® A3EG7 BK23189 Radiflam® A RV350 AF 333 NER 单位测试方法

Dew Point - 热风干燥机 °C

加工熔体温度 °C

干燥时间 hr

干燥时间 - 热风干燥机 hr

干燥温度 °C

干燥温度 - 热风干燥机 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部