PC+PBT，POCAN® C 1202 000000对比PC+PBT，POCAN® C1202LT 904040物性表,价格行情_搜料

牌号信息	POCAN® C 1202 000000 物性表 PC+PBT & 德国恩骅力指导价格：暂无塑料库存：缺货	POCAN® C1202LT 904040 物性表 PC+PBT & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Pocan C 1202 000000 PBT+PC，非增强，注塑，提高冲击强度，低翘曲倾向C 1202 000000 PBT+PC，非增强，注塑，提高冲击强度，低翘曲倾向，紫外线稳定 POCAN® C1202 000000 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp POCAN® C1202 000000 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp POCAN® C1202 000000 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp	PBT+PC，非增强，注塑，提高冲击强度，低翘曲倾向，提高激光透明度，近红外激光透明着色（黑色） POCAN® C1202LT 904040 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, improved laser-transparency, NIR-laser transparent coloring (black) POCAN® C1202LT 904040 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, improved laser-transparency, NIR-laser transparent coloring (black) POCAN® C1202LT 904040 PBT+PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, improved laser-transparency, NIR-laser transparent coloring (black)

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PC+PBT PC+PBT	PC+PBT PC+PBT
填料：
用途：
性能特点：	低翘曲性,冲击性能好,耐候抗UV Low warping,High impact resistance,Weather resistance is good	低翘曲性,冲击性能好 Low warping,High impact resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POCAN® C 1202 000000 POCAN® C1202LT 904040 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(MD：250℃，2.0 mm)
Shrinkage rate %

收缩率(MD：250℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：250℃，2.0 mm)
Shrinkage rate %

收缩率(TD：250℃，2.0 mm)
Shrinkage rate % ISO 2577

熔体体积流动速率(270℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL POCAN® C 1202 000000 POCAN® C1202LT 904040 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178/A

弯曲强度(23℃)
bending strength MPa

弯曲强度(23℃)
bending strength MPa ISO 178-A

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲强度(3.50% 应变，23℃)
bending strength MPa ISO 178-A

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/50

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2/50

冲击性能
IMPACT POCAN® C 1202 000000 POCAN® C1202LT 904040 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL POCAN® C 1202 000000 POCAN® C1202LT 904040 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

补充信息
POCAN® C 1202 000000 POCAN® C1202LT 904040 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

ISO Shortname
ISO Shortname ISO 7792

加工方式

注射 POCAN® C 1202 000000 POCAN® C1202LT 904040 单位测试方法

Residual Moisture Content %

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - 除湿干燥剂 hr

干燥温度 - 除湿干燥剂 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 60x60x2; WZ 70°C; 600 Bar

3 60x60x2mm, 70°C MT, 600 bar

4 0.079 in/min

5 2 mm/min

6 Pull Rate: 2 mm/min; 50% RH

7 10°C/min

2. 60x60x2mm, 70°C MT, 600 bar

3. 2.0 mm/min

4. 2 mm/min

5. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
加工方式
注射
备注