牌号信息	LEXAN™ LUX9130T resin 物性表 PC & 沙特沙伯基础指导价格：38850.0元/吨塑料库存： 23300kg	LEXAN™ LUX9130C resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lux9130T聚碳酸酯（PC）树脂是一种非填充、可注射成型的等级。这种非氯化、非溴化阻燃PC的UL-94V0额定值为1.5 mm/5 VA额定值为6.0 mm，紫外线稳定，提供额外的耐候性。Lux9130T具有高透明度、极低雾度和无气泡性，适用于厚零件成型。Lux9130T有透明和有色两种颜色可供选择，非常适合各种应用。 LUX9130T Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm / 5VA rating at 6.0mm and is UV stabilized providing additional weathering capability. LUX9130T is high transparency, extremly low haze and bubble free for thick part molding. LUX9130T is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications.	Lexan Lux9130c树脂LexanLux9130c聚碳酸酯（PC）树脂是一种非填充、注射成型级树脂。这种非氯化、非溴化阻燃PC具有1.5 mm的UL-94V0额定值，高流动能力，并且紫外线稳定，提供额外的风化能力。LexanLux9130c提供透明和着色的颜色选择，是多种应用的最佳选择。Lexan Lux9130c树脂Lexan Lux9130c聚碳酸酯（PC）树脂是一种非填充、注塑成型等级。这种非氯化、非溴化阻燃PC具有1.5 mm的UL-94V0额定值，高流动能力，并且紫外线稳定，提供额外的风化能力。Lexan Lux9130C提供透明和着色的颜色选择，非常适合各种应用。 Lexan* LUX9130C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. Lexan* LUX9130C is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	通用,厚壁配件（部件）,电气/电子应用领域,照明应用,医疗/护理用品,电子显示器	照明应用
性能特点：	耐候抗UV,透光性好,无卤,阻燃,防火阻燃等级V-2,防火阻燃等级V-0,防火阻燃等级5VA Weather resistance is good,Good Clarity,Halogen free,Flame Characteristics,V-2,V-0,5VA	耐候抗UV,流动性高,无卤,阻燃,防火阻燃等级V-2,防火阻燃等级V-0耐候性 Weather resistance is good,High liquidity,Halogen free,Flame Characteristics,V-2,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

耐候性
Weathering resistance UL 746C

机械性能
MECHANICAL LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ASTM D4812

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 16

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant ASTM ES7-83

相比漏电起痕指数
Compared to the leakage tracing index UL 746

耗散因数(1.1 GHz)
Dissipation factor ASTM ES7-83

阻燃性能
FLAMMABILITY LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.5 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1.5 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.40 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(6.00 mm)
Flame retardant level

光学性能
OPTICAL LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位
UNIT 测试方法
TEST METHOD

透光率(1000 µm)
Transmittance % 内部方法

透光率(2000 µm)
Transmittance % 内部方法

透光率(2540 µm)
Transmittance % ASTM D1003

透光率(3000 µm)
Transmittance % 内部方法

透光率(6000 µm)
Transmittance % ASTM D1003

加工方式

注射 LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位测试方法

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

建议注射量 LEXAN™ LUX9130T resin LEXAN™ LUX9130C resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*3 sp=62mm

7 80*10*3

8 120*10*4 mm

9 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 120*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
光学性能
加工方式
注射
建议注射量
备注