CAB，Tenite™ Butyrate 285E0V16304 Clear, Trsp对比CAB，Tenite™ Butyrate 485E3720008 Clear, Trsp物性表,价格行情_搜料

牌号信息	Tenite™ Butyrate 285E0V16304 Clear, Trsp 物性表 CAB & 美国伊士曼指导价格：暂无塑料库存：缺货	Tenite™ Butyrate 485E3720008 Clear, Trsp 物性表 CAB & 美国伊士曼指导价格：暂无塑料库存：缺货
牌号简介	TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低，表面越硬，耐热性越高，刚性越高，拉伸强度越高，尺寸稳定性越好。增塑剂含量越高，冲击强度越高。Tenite纤维素塑料有天然、透明、精选的橱柜或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素酯285-04含有防臭面具，增塑剂含量为4%。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-04 contains an odor mask and has a plasticizer level of 4%.	以其韧性、硬度、强度、表面光泽、透明度和温暖感等优良的性能平衡而闻名。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低，表面越硬，耐热性越高，刚性越高，拉伸强度越高，尺寸稳定性越好。增塑剂含量越高，冲击强度越高。Tenite纤维素塑料有天然的、透明的、精选的橱柜或烟雾透明片和黑色半透明片。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素酯485-08含有防臭面具和紫外线抑制剂（UVI）。它的增塑剂含量为8%。 Tenite™ cellulosic plastics are noted for their excellent balance of properties including toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 485-08 contains an odor mask and an ultra-violet inhibitor(UVI). It has a plasticizer level of 8%.

产品描述
厂家：	美国伊士曼 Eastman	美国伊士曼 Eastman
类别：	CAB CAB	CAB CAB
填料：
用途：	电子显示器,显示器装饰	体育用品,玩具
性能特点：	机械强度好,透光性好,韧性好,表面光泽度好,可回收,硬度高,低VOC,柔软性好,经增塑 Good Rigidity,Good Clarity,Good flexibility,Good surface appearance,Renewable resources,Good Hardness,Low odor,Soft,Plasticizing	机械强度好,耐候抗UV,透光性好,韧性好,表面光泽度好,可回收,硬度高,低VOC,柔软性好,经增塑 Good Rigidity,Weather resistance is good,Good Clarity,Good flexibility,Good surface appearance,Renewable resources,Good Hardness,Low odor,Soft,Plasticizing
加工条件：

技术参数

物理性能
PHYSICAL Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

冲击性能
IMPACT Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal conductivity coefficient W/m/K ASTM C177

比热(23℃)
specific heat J/kg/℃ DSC

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：23℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

电气性能
ELECTRICAL Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

介电常数(23℃)
Dielectric constant ASTM D150

介电强度(23℃)
Dielectric strength kV/mm ASTM D149

体积电阻率(23℃)
Volume resistivity ohms·cm ASTM D257

耗散因数(23℃ )
Dissipation factor ASTM D150

光学性能
OPTICAL Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542

透光率(1520 µm)
Transmittance % ASTM E308

雾度(1520 µm)
Haze % ASTM D1003

补充信息
Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

加热减量(72 hrs，80℃)
Heating reduction % ASTM D707

可溶性物质损失(23℃)
Loss of soluble substances % ASTM D570

机械性能
MECHANICAL Tenite™ Butyrate 285E0V16304 Clear, Trsp Tenite™ Butyrate 485E3720008 Clear, Trsp 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，23℃)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

备注

1 一般属性：这些不能被视为规格。

2 Conditioned 4 hours at 70°C (158°F)

3 Range: 0.17 to 0.33

1 一般属性：这些不能被视为规格。

2 Conditioned 4 hours at 70°C (158°F)

3 Range: 0.17 to 0.33


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
光学性能
补充信息
机械性能
加工方式
备注