PPO(PPE)+PS，NORYL™ FE1410PW resin对比PPO(PPE)+PS，XYRON™ G701V物性表,价格行情_搜料

牌号信息	NORYL™ FE1410PW resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：48646.5元/吨塑料库存： 525kg	XYRON™ G701V 物性表 PPO(PPE)+PS & 日本旭化成指导价格：暂无塑料库存：缺货
牌号简介	noryl fe1410pw树脂NORYL™ FE1410PW resin是聚苯醚（PPO）和聚苯乙烯（PS）树脂的混合物，含有10%的玻璃增强剂。该树脂适用于注塑成型。NORYL™ FE1410PW resin已开发用于需要改进水解稳定性的流体工程应用。NORYL™ FE1410PW resin已在欧洲和北美以有限的颜色认证可用于高达85摄氏度的饮用水应用。Noryl Fe1410pw树脂NorylFe1410pw树脂是聚苯醚（PPO）和聚苯乙烯（PS）树脂的混合物，含有10%的玻璃增强剂。该树脂适用于注塑成型。noryl fe1410pw树脂已开发用于流体工程应用，需要提高水解稳定性。Noryl Fe1410PW树脂已通过欧洲和北美地区高达85C的饮用水应用认证，颜色有限。 Noryl FE1410PW resin is a blend of polyphenylene Oxide (PPO) and polystyrene (PS) resin that contains 10% glass reinforcement. The resin is suitable for injection molding. Noryl FE1410PW resin has been developed for fluid engineering applications that require improved hydrolytic stability. Noryl FE1410PW resin has been certified for potable water applications up to 85C in Europe and North America in limited colors.	改性PPE 10%填料增强阻燃V-1 Modified PPE 10% Filler reinforced Flame retardant V-1

产品描述
厂家：	沙特沙伯基础 SABIC	日本旭化成 Asahi Kasei
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：	玻璃纤维/玻璃珠 10	玻璃纤维/玻璃珠 10
用途：	饮用水应用
性能特点：	耐水解 Hydrolysis stability	阻燃,防火阻燃等级V-1,防火阻燃等级5VA Flame Characteristics,V-1,5VA
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(2.0 mm)
Shrinkage rate % 内部方法

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

热性能
THERMAL NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-30~65℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电常数(100 Hz)
Dielectric constant IEC 60250

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY NORYL™ FE1410PW resin XYRON™ G701V 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(2.40 mm)
Flame retardant level UL 94

加工方式

注射 NORYL™ FE1410PW resin XYRON™ G701V 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Break

7 80*10*4 sp=62mm

8 80*10*4

9 120*10*4 mm

1 一般属性：这些不能被视为规格。

2 150x150x2 mm

3 4 mm

4 Short Time


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部