TPO（POE），PRE-ELEC® PP 1351对比TPO（POE），PRE-ELEC® PP 1352物性表,价格行情_搜料

牌号信息	PRE-ELEC® PP 1351 物性表 TPO（POE） & 芬兰普宓斯指导价格：暂无塑料库存：缺货	PRE-ELEC® PP 1352 物性表 TPO（POE） & 芬兰普宓斯指导价格：暂无塑料库存：缺货
牌号简介	PRE-ELEC® PP 1351是一种基于聚丙烯的耗散热塑性化合物。通过使用特殊的导电碳黑来实现电损耗。除了10e5-10e8欧姆之间的稳定表面电阻。PRE-ELEC® PP 1351具有良好的机械性能平衡，易于注射成型。典型应用包括注塑耗散静电放电产品，如板条箱、盒子和手提箱。 PRE-ELEC® PP 1351 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 10e5-10e8 ohms. PRE-ELEC® PP 1351 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded dissipative ESD products such as crates, boxes and tote bins.	PRE-ELEC® PP 1352是一种基于聚丙烯的耗散热塑性化合物。通过使用特殊的导电碳黑来实现电损耗。除了稳定的表面电阻在1E5到1E8欧姆之间。PRE-ELEC® PP 1352具有良好的机械性能平衡，易于注射成型。典型应用包括注塑耗散静电放电产品，如板条箱、盒子和手提箱。 PRE-ELEC® PP 1352 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 1e5 to 1e8 ohms. PRE-ELEC® PP 1352 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded dissipative ESD products such as crates, boxes and tote bins.

产品描述
厂家：	芬兰普宓斯 Premix Oy	芬兰普宓斯 Premix Oy
类别：	TPO（POE） Polyolefin Elastomer	TPO（POE） Polyolefin Elastomer
填料：
用途：	容器,装货箱	容器,装货箱
性能特点：	易加工,导电 Excellent Processability,Conductive	易加工,导电 Excellent Processability,Conductive
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位
UNIT 测试方法
TEST METHOD

弯曲模量(4 mm)
Bending modulus MPa ASTM D790

弯曲模量(4 mm)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2

拉伸强度(4 mm)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240

邵氏硬度(邵氏 A)
Shore hardness ISO 868

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-20℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ISO 180

悬臂梁缺口冲击强度(23℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃，4.00 mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 3

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 4

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms IEC 61340-2-3

加工方式

注射 PRE-ELEC® PP 1351 PRE-ELEC® PP 1352 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 标准 B (120°C/h), 载荷2 (50N)

4 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注
返回顶部

TPO（POE），PRE-ELEC® PP 1351对比TPO（POE），PRE-ELEC® PP 1352对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别