PC+ABS，Iupilon® MB2215R对比PC+ABS，PULSE™ 2000 EZ物性表,价格行情_搜料

牌号信息	Iupilon® MB2215R 物性表 PC+ABS & 日本三菱指导价格：暂无塑料库存：缺货	PULSE™ 2000 EZ 物性表 PC+ABS & 美国盛禧奥指导价格：暂无塑料库存：缺货
牌号简介	Iupilon® MB2215R是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® MB2215R的主要特性有: 阻燃/额定火焰可焊 Iupilon® MB2215R is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB2215R are: Flame Rated Weldable	PULSE 2000 EZ 工程树脂在需要高韧性的应用领域具有最好的性能表现，这些应用从单件物品到复杂零部件均有涉及。PULSE 2000 EZ 可以承受极高和极低的温度，在快速的、重复性的温度波动下，也有良好的性能表现。应用领域：仪表板护膝垫仪表板骨架内饰 Overview PULSE™ 2000EZ is a high-heat PC/ABS resin delivering optimized performance for automotive interior component applications. Benefits Easy flow, reduced scrap, and faster cycle times, while enabling thin wall part design for mass reduction. High-impact strength even at low temperature High Heat resistance for demanding automotive interior components Consistent natural white color produces high quality part appearance when used with color concentrates (self coloring) or Trinseo Color Masterbatch Technology Low odor & VOC to meet all global Automotive OEM specifications Applications: Mid (floor)consoles Instrument Panel components Door panel trim Pillars Storage / load floors / glove box

产品描述
厂家：	日本三菱 Mitsubishi	美国盛禧奥 Trinseo
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：		汽车领域的应用,汽车内部装备,汽车仪表板
性能特点：	焊接,防火阻燃等级HB Welding,HB	热稳定性好 Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Iupilon® MB2215R PULSE™ 2000 EZ 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570，ISO 62

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792，ISO 1183-A

密度(--)
Density g/cm³ ISO 1183-1

收缩率
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(230℃，3.8 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(260℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

机械性能
MECHANICAL Iupilon® MB2215R PULSE™ 2000 EZ 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2 7

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(应变，断裂)
Tensile strain % ISO 527-2 8

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2 5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa ISO 527-2 3

拉伸模量(4 mm，注塑成型)
Tensile modulus MPa ISO 527-2

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2

冲击性能
IMPACT Iupilon® MB2215R PULSE™ 2000 EZ 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁冲击强度(-30℃)
Charpy impact strength 16

简支梁冲击强度(23℃)
Charpy impact strength 17

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² 13

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² 14

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

装有测量仪表的落镖冲击(23℃，Peak Energy)
Dart impact equipped with measuring instruments J

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J

热性能
THERMAL Iupilon® MB2215R PULSE™ 2000 EZ 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 19

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 20

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2 22

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 21

阻燃性能
FLAMMABILITY Iupilon® MB2215R PULSE™ 2000 EZ 单位
UNIT 测试方法
TEST METHOD

燃烧速率
Burning rate mm/min FMVSS 302

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 Iupilon® MB2215R PULSE™ 2000 EZ 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

螺杆转速 rpm

注塑成型 Iupilon® MB2215R PULSE™ 2000 EZ 单位测试方法

干燥时间 hr

干燥温度 ℃

模具温度 ℃

熔体温度 ℃

备注

1 一般属性：这些不能被视为规格。

2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

3 模具温度: 140°F, 熔体温度: 500°F, 注塑压力: 2.61E+4 psi

4 0.039 in/min

5 0.079 in/min

6 类型 1, 从边沿, 缺口A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
注塑成型
备注
返回顶部

PC+ABS，Iupilon® MB2215R对比PC+ABS，PULSE™ 2000 EZ对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别