PPO(PPE)+PS，NORYL™ PX0844 resin对比PPO(PPE)+PS，NORYL™ FXN121LG resin物性表,价格行情_搜料

牌号信息	NORYL™ PX0844 resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存： 5600kg	NORYL™ FXN121LG resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Noryl PX0844树脂PPE+PS混合物。未填充的UL94 HB额定值。吸水率低。水解稳定性。尺寸稳定性。根据ISO306，Noryl PX0844树脂Noryl PX0844是一种VICAT B/120为125°C的未填充标准材料。Noryl PX0844具有高耐热性和一致的加工性能。典型的Alnoryl PX0844树脂汽车内饰。高耐热/防潮。一致的可加工性。 PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability.	noryl fxn121lg是一种适用于注塑成型的未填充改性聚苯醚树脂。即使在抛光工具中成型，该树脂也具有独特的低光泽表面外观，使用无氯化、无溴FR添加剂达到V1 UL94等级。fxn121lg有多种颜色可供选择，可能是多种应用的最佳选择，包括手持设备、外壳和显示器。 NORYL FXN121LG is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this resin uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating. FXN121LG is available multiple colors and may be an excellent choice for a wide variety of applications including hand held devices, housings and displays.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：
用途：	汽车内部零件	外壳
性能特点：	易加工,尺寸稳定性好,耐水解,吸水率低,耐高温,防潮 Excellent Processability,Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,High Heat Resistance,Moisture resistance	无卤,阻燃,低光泽,防火阻燃等级V-1 Halogen free,Flame Characteristics,Low Gloss,V-1
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，总能量)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：0~100℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，100 mm跨度)
bending strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(100 mm跨距)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber abraser mg 内部方法

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

电气性能
ELECTRICAL NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(50 Hz)
Relative permittivity IEC 60250

相对电容率(60 Hz)
Relative permittivity IEC 60250

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(50 Hz)
Dissipation factor IEC 60250

耗散因数(60 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(3.2 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

光学性能
OPTICAL NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位
UNIT 测试方法
TEST METHOD

光泽度(60°，无织构)
gloss ASTM D523

加工方式

注射 NORYL™ PX0844 resin NORYL™ FXN121LG resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 0.20 in/min

4 类型 1, 2.0 in/min

5 类型 1, 0.20 in/min

6 0.10 in/min

7 0.051 in/min

8 0.079 in/min

9 Yield

10 80*10*4

11 120*10*4 mm

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
电气性能
阻燃性能
光学性能
加工方式
注射
备注
返回顶部