PAEK，AvaSpire® AV-722 CF30对比PAEK，AvaSpire® AV-621 CF30物性表,价格行情_搜料

牌号信息	AvaSpire® AV-722 CF30 物性表 PAEK & 比利时索尔维指导价格：暂无塑料库存：缺货	AvaSpire® AV-621 CF30 物性表 PAEK & 比利时索尔维指导价格：暂无塑料库存：缺货
牌号简介	AvaSpire AV-722 CF30是AvaSpire AV-722的30%碳纤增强牌号。与30% 碳纤增强PEEK相比，部件具有更具经济性，同时保持了碳纤增强PEEK所具有的高性能优势。这些有用性能包括耐化学性、抗疲劳性以及长期热氧化稳定性。 AV-722 CF30 各性能的出色平衡使之可以用于各行各业广泛的用途，包括医疗保健、交通运输、电子和化学处理。 AV-722 CF30的熔融加工性能非常接近30% CF增强PEEK。 AvaSpire® AV-722 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-722. This formulation offers improved part economics relative to 30% carbon fiber reinforced PEEK while retaining most of the desirable high performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-722 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, oil and gas and chemical processing. The melt processing behavior of AV-722 CF30 is overall very similar to that of 30% CF reinforced PEEK.	AvaSpire AV-621 CF30是AvaSpire AV-621的30% 碳纤增强牌号。尺寸稳定性和抗翘曲性能优于30% 碳纤增强PEEK。韧性和抗冲击强度高于PEEK（聚醚醚酮），在所有AV 621 牌号中，AV-621 CF30具有最高的强度、刚度和抗疲劳性。而且，该树脂同时保留了碳纤增强PEEK所具有的大多数有用的关键性能，包括耐化学性、抗疲劳性、以及长期热氧化稳定性。AV-621 CF30各种性能的出色平衡使之可以用于各行各业广泛的用途，包括医疗保健、交通运输、电子和化学处理。该材料可以在标准设备上很方便地进行熔融加工。AV-621 CF30的熔融加工性能非常接近30% CF 增强PEEK。低流动性AV-621 CF30牌号非常适合挤出用途，同时具有AV-651 CF30所具有的性能. AvaSpire® AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing. This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.

产品描述
厂家：	比利时索尔维 Solvay	比利时索尔维 Solvay
类别：	PAEK PAEK	PAEK PAEK
填料：	碳纤维 30	碳纤维 30
用途：	齿轮,汽车领域的应用,工业应用	泵件,密封件,医疗/护理用品
性能特点：	机械强度好,尺寸稳定性好,阻燃,耐高温,耐化学性 Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Solvent resistance	机械强度好,尺寸稳定性好,阻燃,耐高温,耐疲劳性好,耐化学性 Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance
加工条件：	型材挤出成型 Profile extrusion	机器加工

技术参数

冲击性能
IMPACT AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(--)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(--)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch kJ/m² ISO 180

热性能
THERMAL AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

导热系数
Thermal conductivity coefficient W/m/K ASTM E1530

比热(200℃)
specific heat J/kg/℃ DSC

比热(50℃)
specific heat J/kg/℃ DSC

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

线性热膨胀系数(MD：-50~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

机械性能
MECHANICAL AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/5

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-2/1A/1

泊松比
Poisson's ratio ASTM E132

洛氏硬度(M 级)
Rockwell hardness ASTM D785

物理性能
PHYSICAL AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD：3.2 mm)
Shrinkage rate % ASTM D955

熔体表观粘度(400℃，1000 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(400℃，1000 sec^-1)
Apparent viscosity of melt Pa·s ASTM D3835

熔体质量流动速率(400℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

加工方式

注射 AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 AvaSpire® AV-722 CF30 AvaSpire® AV-621 CF30 单位测试方法

螺杆压缩比

备注

1 一般属性：这些不能被视为规格。

2 5" x 0.5" x 0.125" bars

3 0.20 in/min

4 用于主要部件

1 一般属性：这些不能被视为规格。

2 5" x 0.5" x 0.125" bars

3 0.20 in/min

4 200°C，2小时


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
机械性能
物理性能
加工方式
注射
注射速度
备注
返回顶部

PAEK，AvaSpire® AV-722 CF30对比PAEK，AvaSpire® AV-621 CF30对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别