技术参数
物理性能 PHYSICAL
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
密度
Density
g/cm³
ASTM D792
收缩率(MD)
Shrinkage rate
%
内部方法
收缩率(MD:3.2 mm)
Shrinkage rate
%
ASTM D955
收缩率(TD)
Shrinkage rate
%
内部方法
熔体质量流动速率(250℃,11.6kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(280℃,5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
冲击性能 IMPACT
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
j/m
ASTM D256
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
j/m
ASTM D256
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
j/m
ASTM D4812
悬臂梁无缺口冲击强度(23℃,3.2 mm)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁缺口冲击强度(-30℃,3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃,3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179
落锤冲击(3.2 mm)
Drop hammer impact
J
ASTM D3029
热性能 THERMAL
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
热变形温度(0.45 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
相对温度指数(1.5 mm)
Relative temperature index
℃
UL 746
相对温度指数(1.7 mm)
Relative temperature index
℃
UL 746
相对温度指数(3.0 mm)
Relative temperature index
℃
UL 746
相对温度指数(冲击机械性能)
Relative temperature index
UL 746
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(强度机械性能)
Relative temperature index
UL 746
相对温度指数(电气性能)
Relative temperature index
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525 2
电气性能 ELECTRICAL
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
介电强度(1.5 mm)
Dielectric strength
kV/mm
ASTM D149
介电强度(3.2 mm,在空气中)
Dielectric strength
kV/mm
ASTM D149
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
灼热丝可燃性指数(1.5 mm)
Glowing wire flammability index
热丝引燃(1.5 mm)
Hot wire ignition
UL 746
热丝引燃(1.7 mm)
Hot wire ignition
UL 746
热丝引燃(3.0 mm)
Hot wire ignition
UL 746
热丝引燃(HWI)
Hot wire ignition
UL 746
相比漏电起痕指数(1.50 mm)
Compared to the leakage tracing index
UL 746
高电压电弧起痕速率(HVTR)
High voltage arc marking rate
UL 746
高电压电弧起痕速率(HVTR) (1.50 mm)
High voltage arc marking rate (HVTR) (1.50 mm)
UL 746
高电弧燃烧指数(HAI) (1.5 mm)
High Arc Burning Index (HAI)
UL 746
高电弧燃烧指数(HAI) (1.7 mm)
High Arc Burning Index (HAI)
UL 746
高电弧燃烧指数(HAI) (3.0 mm)
High Arc Burning Index (HAI)
UL 746
阻燃性能 FLAMMABILITY
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
阻燃等级(1.01 mm)
Flame retardant level
UL 94
阻燃等级(1.47 mm)
Flame retardant level
UL 94
阻燃等级(1.50 mm)
Flame retardant level
UL 94
阻燃等级(1.70 mm)
Flame retardant level
UL 94
阻燃等级(2.99 mm)
Flame retardant level
UL 94
阻燃等级(3.00 mm)
Flame retardant level
UL 94
机械性能 MECHANICAL
PRL PPX-FR1
NORYL PX1005X
单位 UNIT
测试方法 TEST METHOD
弯曲强度(3.18 mm)
bending strength
MPa
ASTM D790
弯曲强度(屈服,1.30 mm/min,50 mm跨度)
bending strength
MPa
ASTM D638
弯曲模量(2.60 mm/min,100 mm跨距)
Bending modulus
MPa
ASTM D790
弯曲模量(3.17 mm)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服,3.18 mm)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂,3.18 mm)
Tensile strain
%
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服,3.17 mm)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,3.18 mm)
tensile strength
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量(3.18 mm)
Tensile modulus
MPa
ASTM D638
洛氏硬度(R 级)
Rockwell hardness
ASTM D785