PC，LEXAN™ EXRL2032 resin对比PC，LEXAN™ Homopolymer EXRL2032物性表,价格行情_搜料

牌号信息	LEXAN™ EXRL2032 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Homopolymer EXRL2032 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LEXAN EXRL2032是一种阻燃透明聚碳酸酯，具有无溴无氯阻燃体系，具有良好的流动性和薄壁阻燃性能。它旨在满足各种应用的WEEE/RoHS要求。 LEXAN EXRL2032 is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS requirements for various applications.	LEXAN EXRL2032是一种阻燃透明聚碳酸酯，具有无溴无氯阻燃体系，具有良好的流动性和薄壁阻燃性能。它旨在满足各种应用的WEEE/RoHS要求。 LEXAN EXRL2032 is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS requirements for various applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	薄壁部件
性能特点：	易流动,无卤,阻燃,防火阻燃等级V-0 Good liquidity,Halogen free,Flame Characteristics,V-0	易流动,无卤,阻燃 Good liquidity,Halogen free,Flame Characteristics
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(123~127℃)
Ball pressure test IEC 60695-10-2

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 13

电气性能
ELECTRICAL LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

热丝引燃(HWI)
Hot wire ignition UL 746

相比漏电起痕指数
Compared to the leakage tracing index UL 746

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

阻燃性能
FLAMMABILITY LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃

灼热丝起燃温度(1.5 mm)
Igniting temperature of the hot wire ℃

阻燃等级(1.50 mm)
Flame retardant level UL 94

光学性能
OPTICAL LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位
UNIT 测试方法
TEST METHOD

透光率(2000 µm)
Transmittance % 内部方法

雾度(2000 µm)
Haze % 内部方法

加工方式

注射 LEXAN™ EXRL2032 resin LEXAN™ Homopolymer EXRL2032 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 0.49 in/min

7 Break

8 80*10*3

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)

2. 5.0 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. 13 mm/min

7. at Break

8. 80*10*3 mm

9. 80*10*4 mm

10. 速率 A (50°C/h), 载荷2 (50N)

11. Surface


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
光学性能
加工方式
注射
备注