牌号信息	LIHAN® CT9000 物性表 PC+PBT & 南京立汉指导价格：暂无塑料库存：缺货	VALOX™ 357X resin 物性表 PC+PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	阻燃PC/PBT合金小册子p0lycarbonate（PC）材料具有良好的冲击强度、表面光泽度和自熄性，但其流动性和抗环境应力较差。聚对苯二甲酸乙二醇酯（PBT）具有良好的加工性能和电性能。PC/PBT合金具有轧制成一体的优点。高耐火PC/PBT合金已达到UL-94V-0（0.8毫米）和5VA（2.5毫米），满足欧盟RoHS。该材料已获得跨国电子运营部的认可，并被列为公司全球采购项目之一。该材料可用于电子零件、仪器外壳。 Fire resistance PC/PBT alloy Pamphleti The P0lycarbonate(PC) material has good impact strength, surface glossiness and self-extinguishing, but its fluidity and anti—environmental stress are very poor. The Polyethylene terephthalate (PBT) has good processability and electrical property. The PC/PBT alloy has both advantages rolled into one. High fire resistant PC/PBT alloy has reached UL-94 V-0(O.8mm) and 5VA(2.5mm), and it satisfies the European Commission ROHS. The material has been recognized by multinational electronics operation and listed as one of the company global purchase items. The material can be used to electronic parts, apparatus shell.	Valox 357X是一种冲击改性、火焰重涂PBT+PC混合物。诸如线轴、开关和外壳等应用。 VALOX 357X is an impact modified, flame retarted PBT+PC blend. Applications like bobbins, switches and enclosures.

产品描述
厂家：	南京立汉 Lihan	沙特沙伯基础 SABIC
类别：	PC+PBT PC+PBT	PC+PBT PC+PBT
填料：
用途：	电气元件	线轴,外壳,开关
性能特点：	易加工,表面光泽度好,冲击性能好,电气性好,阻燃,自熄,防火阻燃等级V-0,防火阻燃等级5VA Excellent Processability,Good surface appearance,High impact resistance,Good Electrical Properties,Flame Characteristics,Self-extinguishing,V-0,5VA	冲击性能好,阻燃,防火阻燃等级V-0,防火阻燃等级5VA High impact resistance,Flame Characteristics,V-0,5VA
加工条件：	挤出 Extrusion	注射成型 Injection Molding

技术参数

冲击性能
IMPACT LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA, ISO 179/2C

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度
Hot deformation temperature

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ DSC

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(A50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50 13 22

电气性能
ELECTRICAL LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150，IEC 60250

介电常数(50 Hz)
Dielectric constant IEC 60250

介电常数(60 Hz)
Dielectric constant IEC 60250

介电强度(0.8 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257，IEC 60093

热丝引燃(HWI)
Hot wire ignition UL 746

相比漏电起痕指数
Compared to the leakage tracing index UL 746

相比漏电起痕指数(CTI)
Compared to the leakage tracing index V

相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index V

耐电弧性
Arc resistance ASTM D495

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(50 Hz)
Dissipation factor IEC 60250

耗散因数(60 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

高电压电弧起痕速率(HVTR)
High voltage arc marking rate UL 746

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

阻燃性能
FLAMMABILITY LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(0.75 mm)
Flame retardant level

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(2.50 mm)
Flame retardant level

阻燃等级(2.50 mm)
Flame retardant level UL 94

机械性能
MECHANICAL LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber abraser mg 内部方法

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

物理性能
PHYSICAL LIHAN® CT9000 VALOX™ 357X resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

收缩率(MD)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD)
Shrinkage rate %

熔体体积流动速率(250℃，5 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(265℃，5 kg)
Melt Volume Rate cm³/10min

熔体表观粘度(260℃，1500 sec^-1)
Apparent viscosity of melt Pa·s ISO 11443

熔体质量流动速率(250℃，5.0kg)
Melt Flow Rate g/10min

熔体质量流动速率(265℃，5.0kg)
Melt Flow Rate g/10min

熔体质量流动速率(266℃，5.0kg)
Melt Flow Rate g/10min

加工方式

挤出 LIHAN® CT9000 VALOX™ 357X resin 单位测试方法

熔体温度 °C

注射 LIHAN® CT9000 VALOX™ 357X resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2.0 in/min

4 类型 1, 2.0 in/min

5 0.051 in/min

6 0.079 in/min

7 Yield

8 80*10*4 sp=62mm

9 80*10*4

10 120*10*4 mm

11 80*10*4 mm

12 标准 B (120°C/h), 载荷2 (50N)

13 速率 A (50°C/h), 载荷2 (50N)

14 钨电极


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
电气性能
阻燃性能
机械性能
物理性能
加工方式
挤出
注射
备注
返回顶部

PC+PBT，LIHAN® CT9000对比PC+PBT，VALOX™ 357X resin对比物性表,价格行情_搜料_soliao