PP，LNP™ THERMOCOMP™ MFB22S compound对比PP，SLOVALEN® PC 51 GF 10物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ MFB22S compound 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货	SLOVALEN® PC 51 GF 10 物性表 PP & 斯洛伐克Plastcom 指导价格：暂无塑料库存：缺货
牌号简介	LNP™ THERMOCOMP™ MFB22S是一种基于聚丙烯的化合物，含有10%的玻璃纤维和10%的玻璃珠。该等级的附加特征是：热稳定。也称为：lnpThermocomp化合物mfx-1004 hs-mg产品再订购名称：mfb22s LNP THERMOCOMP MFB22S is a compound based on Polypropylene containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Heat Stabilized.	Lubrione润滑和耐磨化合物被专门配制成自润滑材料，提供低摩擦系数和改进的耐磨性能。润滑油化合物已被证明可以减少摩擦、噪音、振动、热积聚并提高产品的耐久性。 Modified copolymer PP for injection moulding, chemically reinforced with 10% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suitable for automotive, engineering, electrical and consumer goods industry. With the increasing content of GF also the toughness, tensile and bending strength, modulus in tension and bending increase and the shrinkage decreases as well as the heat application increases up to 150°C. Additional drying of the material is not necessary. Delivered in natural mode and in the full RAL colour scale.

产品描述
厂家：	沙特沙伯基础 SABIC	斯洛伐克Plastcom
类别：	PP PP not specified	PP PP not specified
填料：	玻璃纤维/玻璃珠 10	玻璃纤维/玻璃珠 10
用途：		传送机配件,滑轮,滚轴,商务设备,工业应用,汽车领域的应用,印刷机零件,家电部件,消费品应用领域,齿轮,轴承
性能特点：	热稳定性好 Heat Stabilized	低摩擦系数,润滑性,共聚物,耐磨 Low coefficient of friction,Lubricating,Copolymer,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ MFB22S compound SLOVALEN® PC 51 GF 10 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % STM 64 0808

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % STM 64 0808

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL LNP™ THERMOCOMP™ MFB22S compound SLOVALEN® PC 51 GF 10 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT LNP™ THERMOCOMP™ MFB22S compound SLOVALEN® PC 51 GF 10 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ MFB22S compound SLOVALEN® PC 51 GF 10 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B

加工方式

注射 LNP™ THERMOCOMP™ MFB22S compound SLOVALEN® PC 51 GF 10 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 类型 1, 0.20 in/min