PP均聚，Moplen HP500W对比PP均聚，Borealis PP HK060AE物性表,价格行情_搜料

牌号信息	Moplen HP500W 物性表 PP均聚 & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货	Borealis PP HK060AE 物性表 PP均聚 & 奥地利北欧化工指导价格：暂无塑料库存：缺货
牌号简介	Moplen HP500W是聚丙烯均聚物。Moplen HP500W适用于注塑应用，也可作为流动改进剂用于工业化合物中。它有一个非常高的熔体流动速度，窄的分子量分布和它是以丸状供应。有关监管信息，请参阅Moplen HP500W产品管理公告（PSB）。Moplen HP500W不适用于医疗和制药应用。 Moplen HP500W is a polypropylene homopolymer. Moplen HP500W is suitable for injection moulding applications and can also be used in technical compounds as a flow modifier. It has a very high melt flow rate, a narrow molecular weight distribution and it is supplied in pelletized form.	HK060AE是一种特殊的低粘度聚丙烯均聚物，开发用于生产玻璃哑光增强热塑性塑料。该材料也适用于直接LFT压缩和注射成型工艺以及与LGF结合生产PP-GF复合材料的基础树脂，主要用于注射成型工艺。 HK060AE is a special low viscosity polypropylene homopolymer compound developed to fit the production of Glass Matt reinforced Thermoplastics. This material is also suitable as base resin for the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process.

产品描述
厂家：	荷兰利安德巴塞尔 LyondellBasell	奥地利北欧化工 Borealis AG
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	食品容器,汽车领域的应用,薄壁容器,塑料改性	汽车外部零件,汽车电子,汽车仪表板
性能特点：	流动性高,低粘度,窄分子量分布,均聚物 High liquidity,Low Viscosity,Weight distribution,Homopolymer	热稳定性好,均聚物 Heat Stabilized,Homopolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Moplen HP500W Borealis PP HK060AE 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % 内部方法

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Moplen HP500W Borealis PP HK060AE 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(正割)
Tensile modulus MPa ISO 527-2

球压硬度(H 132/10)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Moplen HP500W Borealis PP HK060AE 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(0℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Moplen HP500W Borealis PP HK060AE 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD：-30~80℃)
Linear coefficient of thermal expansion 1/℃ 内部方法

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

加工方式

注射 Moplen HP500W Borealis PP HK060AE 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注