LDPE，AGILITY™ 2001对比LDPE，Lutene® FB0300物性表,价格行情_搜料

牌号信息	AGILITY™ 2001 物性表 LDPE & 美国陶氏指导价格：暂无塑料库存：缺货	Lutene® FB0300 物性表 LDPE & 韩国LG化学指导价格：暂无塑料库存：缺货
牌号简介	AGILITY™ 2001高性能低密度聚乙烯树脂是一种高压低密度聚乙烯树脂，提供了结合高收缩张力和强度的清晰度。主要特点：适用于零售收缩包装的最佳低密度聚乙烯收缩力和起泡光学韧性的完美结合，适用于要求高的应用，符合：美国FDA 21 CFR 177.1520（c）2.2有关完整细节，请参考法规 AGILITY™ 2001 Performance LDPE Resin is a high pressure LDPE resin offering clarity combined with high shrink tension and strength. Main Characteristics: Optimum LDPE for retail shrink packaging Excellent combination of shrink force and sparkling optics Toughness for demanding applications Complies with: U.S. FDA 21 CFR 177.1520(c)2.2 Consult the regulations for complete details	鲁特尼FB0300主要用于挤出机械性能高的吹塑薄膜，用于制造重型包装袋和托盘收缩膜。叶黄素FB0300具有优良的机械性能和高的抗应力开裂性能，适用于重型袋和特殊的底封袋。（叶黄素FB0300不含滑动剂。）应用：重型产品包装、收缩罩、托盘收缩盖、所有类型的工业包装 LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the excellent mechanical properties and high stress cracking resistance make suitable for heavy duty bags and particularity bottom sealed bags. (LUTENE FB0300 contains no slip agent.) Applications: Packing of heavy products, Shrink hoods, Pallet shrink covers, all types of industrial packing

产品描述
厂家：	美国陶氏 DOW	韩国LG化学 LG Chemical
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：		工业应用,包装,薄膜,收缩性薄膜,袋子
性能特点：		抗应力开裂 High ESCR
加工条件：		吹塑薄膜

技术参数

物理性能
PHYSICAL AGILITY™ 2001 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

抗环境应力开裂(F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
AGILITY™ 2001 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

割线模量(1% 正割，MD：51 µm)
Secant modulus MPa ASTM D882

割线模量(1% 正割，TD：51 µm)
Secant modulus MPa ASTM D882

埃尔曼多夫抗撕强度(MD：51 µm)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(TD：51 µm)
Elmandorf tear strength g ASTM D1922

拉伸应变(MD，断裂)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，51 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，51 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服，51 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，51 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，51 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，51 µm)
tensile strength MPa ASTM D882

氮传输速率
Nitrogen transfer rate cm³/m²/24 hr 内部方法

水蒸气透过性
Water vapor permeability g/m²/24 hr 内部方法

膜强度(MD：51 µm)
Membrane strength J/cm³ ASTM D882

膜强度(TD：51 µm)
Membrane strength J/cm³ ASTM D882

膜耐刺穿性(51 µm)
Membrane puncture resistance J/cm³ 内部方法

落锤冲击
Drop hammer impact g ASTM D1709

落锤冲击(51 µm)
Drop hammer impact g ASTM D1709-A

薄膜厚度(测试)
film thickness µm

透氧率
Oxygen permeability cm³/m²/24 hr 内部方法

热性能
THERMAL AGILITY™ 2001 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ DSC

熔融温度(DSC)
Melting temperature ℃ 内部方法

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

光学性能
OPTICAL AGILITY™ 2001 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，50.8 µm)
gloss ASTM D2457

光泽度(60°)
gloss ASTM D2457

雾度
Haze % ASTM D1003

雾度(50.8 µm)
Haze % ASTM D1003

机械性能
MECHANICAL AGILITY™ 2001 Lutene® FB0300 单位
UNIT 测试方法
TEST METHOD

撕裂阻力(MD)
Tear resistance MPa ASTM D1922

撕裂阻力(TD)
Tear resistance MPa ASTM D1922

加工方式

挤出 AGILITY™ 2001 Lutene® FB0300 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 方法 B

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
光学性能
机械性能
加工方式
挤出
备注